Abstract:As HDS catalysts, the supported catalysts including oxide state Mo, Co–Mo and sulfide state Mo on carbon nanotube (CNT) were prepared, while the corresponding supported catalysts on γ-Al2O3 were prepared as comparison. Firstly, the dispersion of the active phase and loading capacity of Mo species on CNT was studied by XRD and the reducibility properties of Co–Mo catalysts in oxide state over CNTs were investigated by TPR while the sulfide Co–Mo/CNT catalysts were characterized by XRD and LRS techniques. Secondly, the activity and selectivity of hydrodesulfurization (HDS) of dibenzothiophene with Co–Mo/CNT and Co–Mo/γ-Al2O3 were studied. It has been found that the main active molybdenum species in the oxide state MoO3/CNT catalysts were MoO2, rather than MoO3 as generally expected. The maximum loading before formation of the bulk phase was lower than 6%m (calculated in MoO3). The TPR studies revealed that that active species in oxide state Co–Mo/CNT catalysts were more easily reduced at relatively lower temperatures in comparison to those in Co–Mo/γ-Al2O3, indicating that the CNT support promoted the reduction of active species. Among 0–1.0 Co/Mo atomic ratio on Co–Mo/CNT, 0.7 has the highest reducibility. It shows that the Co/Mo atomic ratio has a great effect on the reducibility of active species on CNT and their HDS activities and that the incorporation of cobalt improved the dispersion of molybdenum species on CNT and mobilization. It was also found that re-dispersion could occur during the sulfiding process, resulting in low valence state Mo3S4 and Co–MoS2.17 active phases. The HDS of DBT showed that Co–Mo/CNT catalysts were more active than Co–Mo/γ-Al2O3 and the hydrogenolysis/hydrogenation selectivity of Co–Mo/CNT catalyst was also much higher than Co–Mo/γ-Al2O3. For the Co–Mo/CNT catalysis system, the catalyst with Co/Mo atomic ratio of 0.7 showed the highest activity, whereas, the catalyst with Co/Mo atomic ratio of 0.35 was of the highest selectivity.

Influence of Co Oxidation States on Carbon Nanotubes Growth over Co/Mo/MgO

Controlled Growth of Single-Walled Carbon Nanotubes by Catalytic Decomposition of CH4 over Mo/Co/MgO Catalysts

Influence of Mo on the Fe:Mo:C nano-catalyst thermodynamics for single-walled carbon nanotube growth

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

How reduction temperature affects the properites of carbon nanotubes growing over Fe-MgO/Al2O3 catalyst

Water-Assisted Growth of Carbon Nanotubes over Co/Mo/Al_2O_3 Catalyst

Influence of Cerium Metal As Catalyst on the Growth and Structure of Single-Walled Carbon Nanotubes

Co/carbon-nanotube monometallic system: the effects of oxidation by nitric acid

Improvement of Fe/MgO catalysts by calcination for the growth of single- and double-walled carbon nanotubes.

Synthesis of Single-Walled Carbon Nanotubes with Narrow Diameter Distribution by Calcination of a Mo-Modified Fe/MgO Catalyst

Efficient growth of horizontally aligned single-walled carbon nanotubes by chemical vapor deposition over MgO-supported bimetallic co-based catalysts.

Catalytic Chemical Vapor Deposition of Methane to Carbon Nanotubes: Copper Promoted Effect of Ni/MgO Catalysts

Carbon nanotubes-templated assembly of LaCoO3 nanowires at low temperatures and its excellent catalytic properties for CO oxidation

A New Understanding of Carbon Nanotube Growth: Activation and Deactivation of a Catalyst

Mössbauer Study of Catalytically Grown Carbon Nanotube

CVD synthesis of single-walled carbon nanotubes by Co/MgO solid catalysts

Effect of adding nickel to iron–alumina catalysts on the morphology of as-grown carbon nanotubes

Molybdenum anchoring effect in Fe–Mo/MgO catalyst for multiwalled carbon nanotube synthesis

States of Carbon Nanotube Supported Mo-Based HDS Catalysts

Transition Metal (fe2o3, Co3O4 and NiO)-Promoted CuO-Based Α-Mno2 Nanowire Catalysts for Low-Temperature CO Oxidation

Statistical patterns in high-throughput growth of single-wall carbon nanotubes from Co/Pt/Mo ternary catalysts