Abstract:To investigate the durability of reinforced concrete (RC) beams under the combined actions of transverse cracks and corrosion, corrosion tests were conducted on a total of eight RC beams with different water–cement ratios and cracking states. The effects of the transverse crack width, water–cement ratio, and the length of the wetting–drying cycle on the distribution of the free chloride concentration, the cross-sectional loss of the tensile steel bars, and the chloride diffusion coefficient are analyzed. The results show that the widths of the transverse crack and the water–cement ratio of concrete greatly affected the chloride profile and content of the RC beam specimens. Specifically, the chloride contents in all the cracked RC beams at the depth of the steel bar exceeded the threshold value of 0.15%. As the width of the cracks increased, the chloride concentration and penetration of the cracked concrete beam increased. However, the chloride concentration at the reinforcement position did not seem to be obviously affected by increasing the wetting–drying cycles from 182 days to 364 days. Moreover, the decrease of the water–cement ratio effectively inhibited the penetration of chloride ions in the RC beam specimens. In terms of the cross-sectional loss of the steel bars, the average loss of the steel bar increases with increasing crack width for the beams with 182-day cycles, while the effect of crack width on the average loss is not as noticeable for the beams with 364-day cycles. Finally, a model is proposed to predict the relationship between the crack width influence coefficient, μ, and the crack width, w, and this model shows good agreement with the experimental results.

Effect of Cracks in Concrete on Chloride Penetration

Effect of chloride penetration on CFRP sheet, CFRP‐concrete interface, and CFRP‐strengthened concrete beams

Chloride Penetration in Surface-Treated Concrete in Natural and Accelerated Environments

Experiments of chloride ingression in flexural reinforced concrete beams

Effect of Reinforced Concrete Cracking on Chloride Ion Penetration

Comparison of Chloride Penetration into Surface-Treated Concrete in Artificial and Natural Environments

Influence of cracking on chloride diffusivity and moisture influential depth in concrete subjected to simulated environmental conditions

Experimental Study on Chloride Penetration in Cracked Engineered Cementitious Composite under Soak-Dry Cycles

Comparative Study on Clˉ Penetration in Cracked High Ductility and Low Shrinkage Material and Steel Fiber Concrete

Characteristics of Concrete Cracks and Their Influence on Chloride Penetration

Chloride Penetration into Concrete Damaged by Uniaxial Tensile Fatigue Loading

Chloride Transport Behavior in Bending-Shear Section of Reinforced Concrete Beam under Combined Effect of Load and Environment

Influence of Crack Width on Chloride Penetration in Concrete Subjected to Alternating Wetting–Drying Cycles

InfIuence of Ioad crack on chIoride diffusion in concrete

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

The Effect of Crack Width on Chloride-Induced Corrosion of Steel in Concrete

On the Penetration of Corrosion Products from Reinforcing Steel into Concrete Due to Chloride-Induced Corrosion

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Effect of Chloride-Induced Reinforcing Steel Corrosion on the Flexural Strength of Reinforced Concrete Beams

Chloride Penetration in Reinforced Concrete Beams under Combined Sustained Loading and Drying–Wetting Cycles

EFFECT OF FLEXURAL LOADS ON THE CHLORIDE PENETRATION OF CONCRETE