Abstract:Whether the performance of carbon fiber‐reinforced polymer (CFRP)‐strengthened concrete structure is affected by chloride penetration is the key to the application under chloride environments. In this paper, the effect of chloride penetration on tensile properties of CFRP sheet, bond behavior of CFRP‐concrete, and flexural performance of CFRP‐strengthened concrete beams were studied. Results show that chloride penetration has no effect on the elastic modulus of the CFRP sheet. The tensile strength and elongation of the CFRP sheet decrease with the exposure time increase, reducing by 10% and 12.7% after 240 days. The interface failure of CFRP‐concrete is likely to occur on the concrete surface. As the exposure time increases, the interface failure develops toward the epoxy resin layer; the sliding stiffness and end slip of the interface decrease. However, the ultimate bearing capacity of the interface first increases and then decreases. As the exposure time increase, the effective bonding length gradually increases, and the failure mode of CFRP‐strengthened beams changes from bending failure to shear failure. After 120 days, the ultimate bearing capacity of the beams is significantly reduced. From three parts of materials, interfaces, and components to provide an evaluation basis for the use, regular detection, and life prediction of CFRP‐strengthened reinforced concrete beams under chloride environments.

EFFECT OF FLEXURAL LOADS ON THE CHLORIDE PENETRATION OF CONCRETE

Effect of chloride penetration on CFRP sheet, CFRP‐concrete interface, and CFRP‐strengthened concrete beams

Chloride Transport Behavior in Bending-Shear Section of Reinforced Concrete Beam under Combined Effect of Load and Environment

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Study On Relationship Between Chloride Diffusion In Concrete And Time

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

Experiments of chloride ingression in flexural reinforced concrete beams

Chloride Penetration in Surface-Treated Concrete in Natural and Accelerated Environments

Chloride Penetration into Concrete Damaged by Uniaxial Tensile Fatigue Loading

Comparison of Chloride Penetration into Surface-Treated Concrete in Artificial and Natural Environments

Experimental Study On Permeability And Chloride Resistance Properties Of Concrete In Yu-Cheng Bridge

Effect of External Loads on Chloride Transport in Concrete

Durability Of Concrete Under Coupling Effects Of Cyclic Loads And Chloride Environment

The Influence of Long-Term Sustaining Load on the Permeability of Plain Concrete to Chloride Ion

Experimental Study on Chloride Ion Transport in Concrete Structure under Shear Stress

Chloride penetration in concrete exposed to cyclic drying-wetting and carbonation

Experimental investigation on chloride ion of penetration of concrete with flag ash and slag under static bending load

Study on Relation Between Early-age Performance of Concrete and Its Durability

Chloride Transport in Concrete under Sustained Flexural Loading

Chloride Penetrating under Co-Effects of Initial Curing and Exposure Conditions

Effect of Chloride-Induced Reinforcing Steel Corrosion on the Flexural Strength of Reinforced Concrete Beams