Preparation and characterization of alumina hollow fiber membrane

li jiansheng,liu xiaodong,sun xiuyun,wang lianjun,hao yanxia

IF: 16.5

2010-01-01

Chinese Journal of Catalysis

Abstract:The preparation method of alumina hollow fiber membrane by reaction bonding of aluminum oxide (RBAO) technique combined with dry-wet spinning process was introduced in this paper. The reaction behavior, phase transition and microstructure of the membrane were investigated by different techniques, such as thermogravimetric analysis, energy dispersive spectroscopy, X-ray diffraction, thermomechanical analysis and scanning electron microscopy. The structure of alumina hollow fiber membrane is asymmetrical. The porosity and mean pore size of the membrane are 50.1 % and 0.88 μm respectively. The compress strength and bending strength are 89.6 and 41.1 MPa respectively. It was shown that the prepared membrane has high porosity, narrow pore size distribution and improved mechanical properties. The results of permeation test for H2, N2 and Ar exhibited that the membrane is free of defects or cracks and has good permeability.