Abstract:In this work, ultrathin planar alumina-based ceramic membranes with asymmetric structure and thickness less than 0.85 mm were successfully prepared by one-step molding phase transformation/sintering method using low-cost black talc (BT) nanosheets for the first time. The microstructure, pore structure, mechanical strength and permeability of novel ceramic membranes were systematically investigated with different BT amount and sintering temperatures. The doping of BT nanosheets effectively modulated the interfacial bonding area and strength between the grains, achieving significant increase in flexural strength through the evolution of the dense layer structure. The asymmetric structural features formed by the phase transformation/sintering process in combination with polymer substrate significantly reduced the thickness of effective separation layer, thus weakening the loss of flux caused by the densification of the film layer due to the interfacial modification process. Moreover, the organic carbon layers between BT layers were oxidized during the sintering process, forming fine pores and increasing the porosity, which showed to be unique characteristic different from other clay mineral materials. The prepared composite membrane had the pure water flux up to 16335 L m−2 h−1/bar at 1350 °C sintering, which achieved stable permeation of ∼5200 L m−2 h−1/bar and high retention over 90% for O/W emulsions.

Preparation and Properties of Asymmetric Porous Aluminium-Oxide Ceramic Hollow Fibre Membranes

Preparation of a High-Performance Porous Ceramic Membrane by a Two-Step Coating Method and One-Step Sintering

Preparation, characterization and permeation property of Al2O3, Al2O3–SiO2 and Al2O3–kaolin hollow fiber membranes

Preparation and Performance of Polyethersulfone Hollow-Fiber Membrane

Preparation and characterization of alumina hollow fiber membrane

Morphological Characterization of γ-Al 2 O 3 Membranes Fabricated from Ammonium Aluminum Sulphate

A Low-Cost Alumina-Mullite Composite Hollow Fiber Ceramic Membrane Fabricated Via Phase-Inversion and Sintering Method

Asymmetric porous cordierite ceramic membranes prepared by phase inversion tape casting and their desalination performance

Preparation of Al2O3 - SiO2 Composite Membranes Supported on Al2O3 Hollow Fiber

Novel Fabrication Processing of Porous Al2O3/CaAl12O19 Membrane by Combining Emulsion, Cement Curing and Tape-Casting Methods

Preparation and Characterization of Porous Alumina Ceramic Membrane Support

Zeolite Imidazolate Framework Membranes on Polymeric Substrates Modified with Poly(vinyl Alcohol) and Alginate Composite Hydrogels.

A Simple Method for Fabrication of Highly Ordered Porous Alpha-Alumina Ceramic Membranes

Preparation and Characterization of Al<sub>2</sub>O<sub>3</sub>-Based Composite Membranes by Sol-Gel Method

Nanocomposite Mfi-Alumina Hollow Fibre Membranes Prepared Via Pore-Plugging Synthesis: Influence of the Porous Structure of Hollow Fibres on the Gas/Vapour Separation Performance

Low-temperature Sintered High-Strength CuO Doped Ceramic Hollow Fiber Membrane: Preparation, Characterization and Catalytic Activity

Preparation and Characterization of Nanoporous Alumina As Ceramic Membrane Materials

Preparation and properties of PVDF-Al2O3 micro-porous polymer electrolyte membranes

Study on the preparation of gradient-dense Al2O3 hollow fiber membranes by co-sintering process

Preparation and Characterization of Α-Al2o3 Hollow Fiber Membranes with Four-Channel Configuration

Asymmetric alumina-based ultrathin composite ceramic membranes with interfacial modification of black talc nanosheets