Abstract:Catalytic oxidation of sulfite is critical for the fixation of sulfite in the flue gas desulfurization process and is also an essential step related to the treatment of air and water pollution. This work designed and prepared a nano-MnO2-functionalized hydrophobic ceramic membrane with a hydro-phobic surface by a hydrothermal method. The chemical composition and the nanostructure of the prepared MnO2 composite membranes were characterized using several identification techniques (X-ray diffraction, Fourier-transform infrared spectroscopy, Raman spectroscopy, scanning electron microscopy, and X-ray photoelectron spectroscopy). The results show that the prepared nano-MnO2 was sea urchin-like, the crystal form was show that the prepared nano-MnO2 was sea urchin-like, the crystal form was beta-MnO2, and it grows uniformly on the surface of the ceramic membrane. The molar ratios of Mn4+/Mn3+ and Olatt/Ototal were associated with high catalytic activity and enhanced with increasing preparation concentration. The catalytic ability of nano-MnO2 composite membranes to Na2SO3 was studied by the membrane dispersion-catalysis process. The catalytic efficiency with a loaded amount of 1.6-4.5 mg was 5.4-8.3 times higher than that without the catalyst. The free radical quenching experiment showed that SO5 center dot- was identified as the key free radical in the chain reaction. The oxidation kinetics of sulfite were investigated using a membrane dispersion reactor. The results showed that the catalyst, sulfite, and oxygen partial pressure reaction orders were 0.411, 0.243, and 0.640, respectively, and showed an apparent activation energy of 1.89 kJ center dot mol-1. Based on the three-phase reaction model analysis, sulfite oxidation was considered to be controlled by the mass transfer process of oxygen from the gas phase to the liquid phase.

Low-temperature Sintered High-Strength CuO Doped Ceramic Hollow Fiber Membrane: Preparation, Characterization and Catalytic Activity

Fabrication of Catalytic Ceramic Nanofiber Membrane with High Permeability and Superior Catalytic Performance

Preparation of a High-Performance Porous Ceramic Membrane by a Two-Step Coating Method and One-Step Sintering

One-step dip-coating method for preparation of ceramic nanofiber membrane with high permeability and low cost

Preparation and Modification of Ceramic Membrane and Its Application in Oil/Water Wastewater Treatment

Preparation of Ceramic Ultrafiltration Membrane by Nano-Metal Oxides Modified

A Low-Cost Alumina-Mullite Composite Hollow Fiber Ceramic Membrane Fabricated Via Phase-Inversion and Sintering Method

Modulating the Bactericidal Activity and Corrosion Resistance of Al2O3 Porous Ceramics Through Cu and Fe Co-Introduction for Membrane Support Application

High-performance Macro-Porous Alumina-Mullite Ceramic Membrane Supports Fabricated by Employing Coarse Alumina and Colloidal Silica

Asymmetric alumina-based ultrathin composite ceramic membranes with interfacial modification of black talc nanosheets

Preparation and Properties of Asymmetric Porous Aluminium-Oxide Ceramic Hollow Fibre Membranes

CuO-Fe3C-C Modified PVDF Membrane for Catalysis and Antifouling

Novel Fabrication Processing of Porous Al2O3/CaAl12O19 Membrane by Combining Emulsion, Cement Curing and Tape-Casting Methods

Integrated preparation of alumina microfiltration membrane with super permeability and high selectivity

Enhanced Mechanical Strength and Bactericidal Activity of Macro-Porous Al2O3 Ceramics Through the Introduction of Cu for Membrane Support Application

Efficient Activity of CoCu@SiC Catalytic Ceramic Membrane Via H2 Reduction Treatment for Pollutants Degradation

Cost-effective Tubular Cordierite Micro-Filtration Membranes Processed by Co-Sintering

Processing and microstructure-permeation properties of silica bonded silicon carbide ceramic membrane

Development of CuO Coated Ceramic Hollow Fiber Membrane for Peroxymonosulfate Activation: a Highly Efficient Singlet Oxygen-Dominated Oxidation Process for Bisphenol a Degradation

Melded Ceramic Membranes: A Novel Fabrication Method for Ultrathin Alumina Membranes of High Performance

MnO2-Functionalized Hydrophobic Ceramic Membrane for Sulfite Oxidation