Analysis of Tertiary Oxide Scale with Different Hot Rolling Processes Parameters

SUN Bin,CAO Guang-ming,LIU Zhen-yu,WANG Guo-dong
DOI: https://doi.org/10.13228/j.boyuan.issn1001-0777.2010.06.003
2010-01-01
Abstract:The effort on the structure and thickness of tertiary oxide scale from different initial rolling temperatures,finish rolling temperatures and coiling temperatures was studied using thermal simulation machine.The results showed that with the rising of with initial rolling and finish rolling temperature,the proportion of Fe2O3 and Fe3O4 decreased gradually,while the growth rate of FeO was fast.The hysteresis phenomenon of oxide scale is very common,and 350~500 ℃ should be the zone of eutectoid temperature for the experimental steel.One of the effective methods to control proeutectoid and promote was rapid cooling from high region to nose and slow cooling from nose to room in practical production.Less acid wash steel containing more FeO was obtained with the cooling tempreture above the nose temperature,and this kind of oxide scale was beneficial to pickling.And wash steel acid free containing more FeO was available at the nose tempreture.The above were two main thoughts of controlling hot rolling oxide scale.
What problem does this paper attempt to address?