Abstract:When the severity of high-temperature environments increases, the oxidation mode changes from a normal oxidation mode, when a formed oxide layer protects the surface of austenitic heat-resistant cast steels, to an extreme mode, when scale spallation and partial vaporization intensify surface degradation. These processes can also influence each other. On the example of two oxidized austenitic heat-resistant steels with different alloying levels, we show how the described simulation/experimental methodology may be applied to analyze and quantify the synergetic kinetics of the extreme surface degradation processes. The surface degradation processes were formulated using diffusion-controlled parabolic oxidation, time-dependent vaporization, and spallation with an intensity cross-linked to the instantaneous thickness of the oxide layer. The 400 h tests were performed in air and water vapor-containing combustion gases at upper working temperatures. Three experimentally obtained surface degradation quantities included changing the weight of the specimen with adherent oxide, the weight of the spalled scale, and the thickness of the formed adherent oxide. These experimental quantities were used to compute the values of oxidation, vaporization, and spallation kinetic constants for each uninterrupted oxidation test. An additional interrupt every 100-h test was also performed to verify the model-predicted trends. It was shown that the alloying level in austenitic heat-resistant cast steel determines its ability to withstand surface degradation at extreme oxidation mode by the synergetic effects of oxidation, vaporization, and spallation. The described approach can be used for the metallic component lifetime prediction in severe gaseous environments.

Oxidation Kinetics and Spallation Model of Oxide Scale during Cooling Process of Low Carbon Microalloyed Steel

Isothermal Structure Transformation and Kinetics Behavior of Oxide Scale on Low Carbon Steel

Numerical Simulation of Oxide Scales Evolution During Hot Strip Rolling

A Study of the Mechanism of Formation of Composite Oxide Scale on Heat-Resistant Steel 25Cr18Ni9Si2

Experimental Study on Adhesion of Oxide Scale on Hot-Rolled Steel Strip

Factors Affecting the Development of Oxide Scales on Austenitic Stainless Steels during Hot Rolling in Steckel Mills

On the spallation of oxide scales in high-strength low-alloy (HSLA) hot-rolled steels

Descaling Abilities of Two Low-Alloy High-Strength Steels Under Different Heating Processes

In-situ Observation of Cracking and Healing Behavior of High-carbon Steel During Oxide Scale Growth

Investigation of Selective Oxidation During Cooling of Hot-Rolled Iron-Manganese-silicon Alloys

Oxide scale characterization of ferritic stainless steel and its deformation and friction in hot rolling

Understanding of failure mechanisms of the oxide scales formed on nanocrystalline coatings with different Al content during cyclic oxidation

Synergetic Kinetics of High-Temperature Surface Degradation Processes in Austenitic Heat-Resistant Cast Steels

Effect of Oxide Scale Microstructure on Atmospheric Corrosion Behavior of Hot Rolled Steel Strip

Mechanism of Oxidation of Austenitic Stainless Steels under Conditions of Hot Rolling in Steckel Mills

Investigation of breakaway oxidation kinetics of nickel-base single crystal superalloys: Modeling and experiments

Effect of microstructure and microtexture evolution of oxide layer over J82B steel on mechanical descaling properties

Phase Transformation Behavior Of Oxide Scale On Plain Carbon Steel Containing 0.4 Wt.% Cr During Continuous Cooling

Microstructural and microtextural characterization of oxide scale on steel using electron backscatter diffraction

Machine Learning Model for Thickness Evolution of Oxide Scale During Hot Strip Rolling of Steels

Investigation of oxide scale on ferritic stainless steel B445J1M and its tribological effect in hot rolling