Abstract:This research focuses on the influence of silicon alloys in hot-rolled steel strips. The steel used in the study was obtained from a hot rolling process with different silicon contents of 0.01, 0.1, 0.2, and 0.3 wt.%. The as-received oxide scale on the hot-rolled steel surface was completely removed by SiC paper and re-oxidized in a horizontal furnace with an atmosphere of 17% H2O-N2 at temperatures of 600°C, 650°C, and 700°C for 10 seconds. An investigation of scale adhesion can be done using a tensile testing machine with a CCD camera. The adhesion of the oxide scale to the steel surface was recorded on video. The oxide phase was examined by means of X-ray diffraction (XRD). The microstructure and thickness of the oxide scale were examined by a scanning electron microscope (SEM) with energy-dispersive X-ray spectroscopy (EDS). The results indicated that all steels studied produced oxide scales that consisted of hematite (Fe2O3) and magnetite (Fe3O4), which contained iron (Fe). The scale thickness tends to increase with increasing temperature, while thickness decreases with increasing Si content in steel. The oxide scale adhesion was indicated by the strain initiating the first spallation during tensile load. The results showed that the strain initiating the first scale spallation tends to decrease with increasing temperature, while scale adhesion increases with increasing Si content in steel. The mechanical adhesion of the oxide scale to the steel substrate was considered in terms of energy. The results indicate that the scale adhesion of steel with 0.3 wt.% Si was higher than that in another sample. It was possible that the presence of an oxide that contains Si at the scale-steel interface, which encourages scale adhesion. The mechanical adhesion energy of the oxide scale was shown in the range of 2-20 J/m2. The qualitative assessment of scale adhesion in terms of strain initiating the first spallation and mechanical adhesion energy suggested the good adhesion behavior of scale grown in the hot-rolled steel with 0.3 wt.% Si. This result indicates that scale formed on steel with a high silicon content tends to be difficult to remove. There was a need to control the Si content in the hot-rolled steel in a satisfactory way to save energy during the de-scale process.

Descaling Abilities of Two Low-Alloy High-Strength Steels Under Different Heating Processes

Effect of microstructure and microtexture evolution of oxide layer over J82B steel on mechanical descaling properties

Phase Transformation Behavior Of Oxide Scale On Plain Carbon Steel Containing 0.4 Wt.% Cr During Continuous Cooling

Isothermal Structure Transformation and Kinetics Behavior of Oxide Scale on Low Carbon Steel

Influence of Silicon on Oxidation and Adhesion of Oxide Scale on Hot-Rolled Steel Strips

A Study of the Mechanism of Formation of Composite Oxide Scale on Heat-Resistant Steel 25Cr18Ni9Si2

Structural transformation behavior of oxide scale during coiling of 0.9 wt% Cr-containing high-strength steel

Experimental Study on Adhesion of Oxide Scale on Hot-Rolled Steel Strip

High-Temperature Oxidation Behavior of Fe-1Cr-0.2Si Steel

Distinct Oxidation Behaviour Attributed to Phase Constitution Transformation at Different Hot Processing Temperatures in Fe-10Mn-5.5Al-0.25C Steel

Effect of aluminium and silicon on high temperature oxidation resistance of Fe-Cr-Ni heat resistant steel

High-temperature oxidation behavior and subsurface phase transformation of high-Mn high-Al steel

Adhesion of thermal oxide scale formed on silicon-containing hot-rolled steel oxidised in oxygen

Influence of Al on Scale Formation and Growth Kinetics of 10 Wt.% Cr Creep Resistant Ferritic Steels at 650 °C in Air

Oxidation Kinetics and Spallation Model of Oxide Scale during Cooling Process of Low Carbon Microalloyed Steel

Effect of post-annealing on the oxidation behavior of hot rolled ODS-FeCrAl steel in liquid lead

Oxidation behavior of AlCoCrFeNiSi high-entropy alloys at 1100 °C

Effect of cooling route on microstructure and mechanical properties of twin-roll casting low carbon steels with an application of oxide metallurgy technology

Contribution of Sc Doping to the Growth and Adhesion of Alumina Scale on AlCoCrFeNi High-Entropy Alloy

Influence of Si Content on Selective Oxidation and Oxide Scale Phase Transition During Hot-Rolled Coiling

The influence of annealing temperature on the microstructure and mechanical properties of Fe-0.52C-11Mn-5.14Al-1Cr lightweight Steel