Abstract:This article presents an investigation into the effects of natural seawater and sea sand on the behaviour of unconfined and fibre-reinforced polymer-confined concrete. The experimental programme covered compression tests of a large number of standard concrete cylinders, which were prepared from the following four series of concrete: (1) the reference normal concrete, (2) sea-sand concrete, (3) seawater concrete (SwC), and (4) seawater sea-sand concrete. The concrete cylinders were either unconfined or confined with externally wrapped carbon fibre-reinforced polymer jackets to be tested at various ages from the early to the long term. This article presents the results of the first-phase tests, which covered a total of 48 specimens from the four series of concrete, with a half of them tested in the unconfined condition at the ages of 7 and 28 days, and another half tested with either one-ply or two-ply carbon fibre-reinforced polymer jackets at 28 days. The results show that at the ages of 7 and 28 days, the unconfined concrete specimens prepared with seawater and/or sea sand developed a slightly higher compressive strength, as compared to those prepared from normal concrete. When confined with carbon fibre-reinforced polymer jackets, the compressive stress–strain responses of concrete with or without seawater and/or sea sand were very similar. The use of seawater and sea sand did not seem to have significant effects on the compressive strength, ultimate axial strain and stress–strain responses of confined concrete, and the ultimate strain capacity of carbon fibre-reinforced polymer jackets neither. The test results were also compared with the predictions of an existing analysis-oriented stress–strain model for fibre-reinforced polymer-confined concrete. It is shown that the compressive strength, ultimate axial strain, stress–strain responses and dilation behaviour of the carbon fibre-reinforced polymer-confined concrete with or without seawater/sea sand can be reasonably well predicted.

Durability test on the flexural performance of seawater sea-sand concrete beams completely reinforced with FRP bars

Effects of Natural Seawater and Sea Sand on the Compressive Behaviour of Unconfined and Carbon Fibre-Reinforced Polymer-Confined Concrete

The durability of seawater sea-sand concrete beams reinforced with metal bars or non-metal bars in the ocean environment

Durability of BFRP bars and BFRP reinforced seawater sea-sand concrete beams immersed in water and simulated seawater

Durability of glass FRP bar‐reinforced seawater–sea sand concrete beams under sustained loading in a subtropical coastal environment

GFRP bar-reinforced seawater sea-sand concrete beam under the combined influence of seawater exposure and sustained load: Durability and degradation mechanism

Durability of SFCB Reinforced Low-Alkalinity Seawater Sea Sand Concrete Beams in Marine Environment

Durability of Seawater Sea Sand Concrete Beams Reinforced with Carbon Nanotube-Modified BFRP Bars in a Marine Environment

Durability of CFRP-confined seawater sea-sand concrete (SSC) columns under wet-dry cycles in seawater environment

Shear behavior of seawater sea-sand concrete beams reinforced with BFRP bars after seawater dry-wet cycling

Flexural performance of FRP-SWSSC-steel composite beams: Experimental and analytical investigation

Long-Term Durability of Basalt- and Glass-Fibre Reinforced Polymer (bfrp/gfrp) Bars in Seawater and Sea Sand Concrete Environment

Effect of sustained load and seawater and sea sand concrete environment on durability of basalt- and glass-fibre reinforced polymer (B/GFRP) bars

Evaluation of Deformation for Steel Fiber Concrete Beams with BFRP Tendons Eroded by Seawater under Cyclic Loading

Flexural Performance of Seawater Sea Sand Concrete Composite Beams Enhanced by Dual-Functional C-FRCM Jackets

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Bond durability and degradation mechanism of GFRP bars in seawater sea-sand concrete under the coupling effect of seawater immersion and sustained load

Relationships Between Interfacial Behavior and Flexural Performance of Hybrid Steel-Frp Composite Bars Reinforced Seawater Sea-Sand Concrete Beams

Durability Study On Interlaminar Shear Behaviour Of Basalt-, Glass- And Carbon-Fibre Reinforced Polymer (B/G/Cfrp) Bars In Seawater Sea Sand Concrete Environment

Shear behaviour of seawater sea-sand coral aggregate concrete beams reinforced with FRP strip stirrups

Experimental Investigation on the Bond Performance of Sea Sand Coral Concrete with FRP Bar Reinforcement for Marine Environments