Abstract:In order to study the mechanical properties of seawater sea sand concrete and the durability damage law of seawater sea sand concrete under the action of seawater erosion, corresponding specimens were prepared and subjected to cube compressive strength, flexural strength, and dry-wet cycle tests by taking the volume dosage of glass fibers and polyvinyl alcohol fibers as variables. The test combined SEM scanning and EDS to analyze the microstructure of fiber-reinforced seawater sand concrete, and established a model based on the two-parameter Weibull probability distribution. The results show that the fiber has a significant effect on improving the mechanical properties and erosion resistance of seawater sand concrete. When the total volume content is 0.3% and the mixing ratio is 1:1, the improvement effect is the best. The maximum increase in cubic compressive strength was 24.2%; the maximum increase in flexural strength was 38.8%. After the specimens were subjected to wet and dry cycles for 360d, the maximum reduction in mass loss rate was 41.23%; the maximum reduction in strength loss rate was 27.55%. As observed from the microscopic images, the main disadvantage of SSC is that the salt crystallization and swelling matter produced by the erosion ions will weaken the bond between aggregate and mortar, resulting in defects in the interfacial transition zone (ITZ). Under the action of dry-wet cycles, the alternating dry-wet forces, the expansion pressure generated by expansive substances and the crystallization pressure generated by salt crystallization will change the microstructure, and therefore the damage of the specimen will deepen with the extension of erosion time. The microscopic images also show that the doping fibers can improve the internal integrity and compactness of the matrix, thus significantly improving the mechanical properties and durability of seawater sea sand concrete. In this test, a damage model was established based on the two-parameter Weibull distribution model, and the damage law between strength loss and dry-wet cycles was fitted, which provides a favorable basis to study the damage of seawater sea sand concrete under wet-dry cycling.

Durability of CFRP-confined seawater sea-sand concrete (SSC) columns under wet-dry cycles in seawater environment

Effects of Natural Seawater and Sea Sand on the Compressive Behaviour of Unconfined and Carbon Fibre-Reinforced Polymer-Confined Concrete

Axial Compressive Behavior and Load Carrying Capacity Prediction of Prefabricated UHPC Tube Filled with Seawater Sea-Sand Coral Aggregate Concrete

Experimental research on compressive behavior of seawater and sea sand concrete-filled RPC tubes

Seismic Performance Of Seawater And Sea Sand Concrete-Filled Ultra-High Performance Concrete Tubes Under Low-Cycle Reversed Lateral Loading

Effect of compression casting method on the axial compressive behavior of FRP-confined seawater sea-sand concrete columns

Durability of BFRP bars and BFRP reinforced seawater sea-sand concrete beams immersed in water and simulated seawater

Durability of Frp Concrete Bonds and Its Constituent Properties under the Influence of Moisture Conditions

Experimental Study on Dynamic Response of CFRCM Confined Seawater Sea Sand RC Columns Subjected to Lateral Impact

Durability Performances of Carbon Fiber-Reinforced Polymer and Concrete-Bonded Systems under Moisture Conditions

Influence of seawater sea sand concrete environment on the long‐term tensile properties of pultruded basalt and basalt‐carbon‐hybrid fiber reinforced polymer profiles

Durability of glass FRP bar‐reinforced seawater–sea sand concrete beams under sustained loading in a subtropical coastal environment

Axial Compressive Behavior and Model Assessment of FRP-confined Seawater Sea-sand Concrete-Filled Stainless Steel Tubular Stub Columns

Study on mechanical properties and anti-erosion performance of fiber reinforced seawater sea sand concrete

CFRP Strengthened RC Beams with Pre-Strengthening Non-Uniform Reinforcement Corrosion Subjected to Post-Strengthening Wetting/drying Cycles

Effect of seawater and stress coupling on the durability of carbon fibre-reinforced polymer

Durability and microstructure degradation mechanism of FRP-seawater seasand concrete structures: A review

Axial compression behaviour of seawater sea sand concrete columns reinforced with hybrid FRP-stainless steel bars

Compressive behavior of FRP-confined normal concrete or seawater sea-sand concrete containing FRP-bar recycled coarse aggregates

Seawater sea-sand concrete columns using durable and ductile steel-FRP composite bars and FRP ties: A promising hybrid scheme for marine engineering

Experimental study on concrete-filled steel tube columns with inner distributed seawater and sea sand concrete-filled fiber-reinforced polymer tubes under axial compression