The Phase Formation Mechanism of Nb3Al Prepared by Mechanical Alloying and Subsequent Sintering and Its Effect on Superconducting Properties

Xin Wen,Xinhua Li,Huanhuan Zhao,Zongqing Ma,Liming Yu,Chong Li,Chenxi Liu,Qianying Guo,Yongchang Liu

DOI: https://doi.org/10.1016/j.intermet.2018.10.001

IF: 4.075

2018-01-01

Intermetallics

Abstract:Nb3Al superconductors with high superconducting performance are of interest as potential materials for using in high magnetic fields. The phase formation mechanism plays a vital role in preparing high quality Nb3Al superconductor, especially with better superconducting transition temperature (T-c). In this work, the phase evolution of Nb-Al system during mechanical alloying and subsequent sintering process was studied, and the corresponding kinetics mechanism of Nb3Al phase formation was investigated in detail. It was found that the Nb3Al phase can be formed through two different routes: one is reaction between Nb2Al and Nb, the other is transformation from Nb-Al supersaturated solid solution (Nb(Al)(ss)) directly. Mechanical alloying promotes the transformation of Nb-Al pre-alloyed powders from local Nb-Al amorphous to Nb(Al)(ss), controlling the different formation routes of Nb3Al phase. According to the kinetics calculation of the Nb3Al phase formation during sintering process, the values of activation energy (E) for the reaction between Nb2Al and Nb forming Nb3Al is higher than that for the transformation from Nb(Al)(ss) to Nb3Al in the initial stage, but decreases sharply with the reaction going on. Moreover, Nb3Al bulk synthesized via reaction between Nb2Al and Nb obtained a higher value of T-c(about 15.8 K) compared with the Nb3Al bulk synthesized via Nb(Al)(ss). The results in our work suggest that the phase formation mechanism of Nb3Al during mechanical alloying and subsequent sintering process actually influence their final superconductivity performance and can give an effective guide for optimizing the technique of preparing Nb3Al superconductors.