Study on the property and microstructure of NbTiTa superconducting wire
Yanmin Zhu,Qiang Guo,Pingxiang Zhang,Kailin Zhang,Ruilong Wang,Zijing Zhou,Luyang Han,Jixing Liu,Wei Xie,Bo Wu,Jianfeng Li,Xianghong Liu,Yong Feng
DOI: https://doi.org/10.1140/epjs/s11734-024-01366-1
2024-10-30
The European Physical Journal Special Topics
Abstract:NbTi superconducting Wire exhibits the advantages of excellent processing characteristics, stable superconducting properties and low cost. It has been widely applied and extensively used for low magnetic fields of < 9 T. To expand the application range in higher magnetic fields, it is vital to improve the upper critical fields ( H c2 ) and the critical current density ( J c ) at high magnetic fields (≥ 9 T) of NbTi superconducting material. This study aims to add Ta element, obtaining both higher J c and higher upper critical fields ( H c2 ). After the addition of Ta element, the critical current density of NbTiTa superconducting wire reaches 681.3, 527.5, and 381.4 A/mm 2 at (4.2 K, 9 T), (4.2 K, 9.5 T) and (4.2 K, 10 T), respectively and the upper critical field H c2 is also higher than that of NbTi superconducting wire. In addition, the NbTiTa superconducting wire also exhibits the striking second magnetization peak effect at high fields, and the flux pinning mechanism changes from the surface pinning at low fields to the Δκ pinning at high fields. This study demonstrates that the NbTiTa superconducting wire can expand the application range in higher magnetic fields (≥ 9 T) by improving the critical current density at high magnetic fields (≥ 9 T) and the upper critical fields of the NbTi superconducting wire.
physics, multidisciplinary