Abstract:In this study, structural, morphological, thermal and magnetic properties of amorphous-nanocrystalline Fe 70 Cr 10 Nb 10 B 10 (at.%) alloy are discussed. The formation and evaluation of amorphous-nanocrystalline structures of the alloy were followed by XRD, SEM-EDX, TEM, DTA, and VSM techniques. After 50 h of milling Cr, Nb, and B were completely dissolved into the Fe lattice forming 82% of the amorphous phase of the alloy. A gradual dissolution of the alloying elements also increased the lattice parameters concurrently. The lattice parameters reached a maximum value of 2.908 Å after 20 h of milling and then leveled off to a value of 2.891 Å at the end of 50 h of milling. Based on the XRD data, crystallite size and lattice strain of the alloy were calculated as 3.2 nm and 3.34% respectively. TEM analyses revealed that the alloy particulates comprised needle-shaped nanoparticles of an average size of 21 nm. The room temperature magnetic hysteresis loops showed that the increased duration of milling decreased the saturation magnetization from 91 to 24 emu/g. This was mainly due to the upsurge on the amorphous phase content in the alloy as the milling progressed. The increase in amorphous phase content and the subsequent reduction of the saturation magnetization were due to the inter-diffusion of the non-ferromagnetic Cr and B atoms into the Fe lattice. Thermal studies revealed that around 350 °C the amorphous phase of the alloy began crystallizing. The magnetic saturation of the heat-treated alloy also increased with the growth in the crystalline phases. The 50 h milled sample annealed at 700 °C was found to have the highest magnetic anisotropy as observed from the temperature-dependent zero-field cooled and field cooled magnetization measurements. The high-pressure X-ray diffraction measurements revealed that the amorphous state of the alloy remained stable up to 11.3 MPa. It also revealed the structural similarities of the Fe 70 Cr 10 Nb 10 B 10 alloy with those of the Fe 70 M 10 B 20 (M = Nb and Cr) types. For all practical purposes, the microstructural stability under high compressive pressure represents the consolidation properties of the nanostructured magnetic materials since both pressure and temperature-induced phase transformations are the primary controlling factors for the specific magnetization properties of the alloy.

Morphology and Phase Constituents of Mechanically Alloyed Nb-Ti-Si Based Ultrahigh Temperature Alloy Powders

Investigation of a Hot-Pressed Nb–Ti–Al Alloy: Mechanical Alloying, Microstructure and Mechanical Property

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

Preparation of Ti/Al based nanophase composite powder by mechanical alloying

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

Eff ects of Diff erent Mechanical Alloying Parameters on Microstructure of High Temperature Nanocrystalline Cu-Ta Alloys

Preparation of ti-al based nanophase composite powder by mechanical alloying

Polymorphic transformation and elemental diffusional controlled phase spheroidization of eutectic VNbTiSi medium entropy alloy during heat treatment

Synthesis and characterization of amorphous-nanocrystalline Fe70Cr10Nb10B10 powders by mechanical alloying

Synthesis of Ultrafine Fe-W-Al-Ti-Ni-C-B Powders by Mechanical Alloying

Study on mechanical alloying behavior and thermal stability of HfMoNbTaTi refractory high-entropy alloy

Phase Transformation of Niti Shape Memory Alloy Powders Prepared by Ball Milling

Enhanced Hot Workability of Ti–46Al–4Nb–0.1B Alloy by Introducing Adjustable β Phase via Elemental Powder Metallurgy

Microstructure and Mechanical Properties of the Powder Metallurgy Nb-16Si-24Ti-2Al-2Cr Alloy

EFFECTS OF HIGH-ENERGY BALL MILLING ON THE STRUCTURE AND PROPERTY OF A MULTIPHASE Al3Ti-BASED INTERMETALLIC ALLOY

Nanocrystalline/Amorphous Tuning of Al–Fe–Nb (Mn) Alloy Powders Produced via High-Energy Ball Milling

Microstructural evolution and thermal stability in a nanocrystalline lightweight TiAlV0.5CrMo refractory high-entropy alloy synthesized by mechanical alloying

Atomic diffusion and microstructural evolution at the Nb/TiAl heterogenous interfaces during annealing at elevated temperatures

Phase Transformation and Morphology Evolution of Ti50Cu25Ni20Sn5 during Mechanical Milling

Effect of Ti and Al on Microstructure and Partitioning Behavior of Alloying Elements in Ni-based Powder Metallurgy Superalloys