Effects of BN on the microstructural evolution and mechanical properties of BAS-BN composites

Qian Li,Delong Cai,Zhihua Yang,Xiaoming Duan,Daxin Li,Yangshan Sun,Shengjin Wang,Dechang Jia,Bollmann Joachim,Yu Zhou

DOI: https://doi.org/10.1016/j.ceramint.2018.10.039

IF: 5.532

2019-01-01

Ceramics International

Abstract:BAS-BN ceramic composites were synthesized by hot-press sintering at 1500 °C with various BN doping contents of 10–50 wt%. The influences of BN on the phase composition, microstructure and mechanical properties of the composite ceramics were studied. Results showed that the addition of BN significantly affected the hexagonal → monoclinic phase transformation of BAS. Single celsian was noted at BN content of 10 wt%, while a mixture of hexacelsian, celsian and some amorphous phase was obtained as BN additions beyond 20 wt%. With the increase in BN contents, nearly a fully dense composite was obtained when the BN content was lower than 30 wt%. And the mechanical performance of the composites was significantly improved. For ceramics with an addition of 30 wt% BN, the flexural strength and fracture toughness reached the maximum values, which was 193.5 MPa and 2.57 MPa m1/2, respectively. And the bending strength is more than twice higher than that of pure BAS ceramic.