Abstract:The low-cycle fatigue of strongly-textured Mg alloys is dominated mainly by an alternation of twinning-detwinning process, which poses a great challenge to conventional constitutive models. As a result, a good reproduction of both mechanical response and deformation behavior often fails in previous simulations, in particular for high strain amplitudes. In the present study, the numerical simulations of low-cycle fatigue behavior of an Mg AZ31 plate with a ± 2% axial strain amplitude along the rolling direction were conducted, using a modified crystal-plasticity based on the finite strain elastic-viscoplastic self-consistent model containing twinning and detwinning mechanisms (EVPSC-TDT), and the results were compared with the mechanical response and deformation behavior determined by a real-time in-situ neutron diffraction. The simulations well predict the hysteresis loops and cyclic-hardening responses throughout the whole fatigue life (80 cycles), along with the evolution of the maximum twin volume fraction and residual twins. For the first time, the evolution of lattice strain throughout the whole fatigue life was calculated, and the results are in good accordance with that determined by neutron diffraction. The present study strongly demonstrates that the EVPSC-TDT model is very effective for modeling the low-cycle fatigue behavior of Mg alloys. More details about the evolution of the maximum twin volume fraction with fatigue cycles are found, an increase from 1st to 2nd cycle, followed by a decrease from 2nd to 20th cycle and a secondary increase after 20th cycle. This finding corrects the previous opinion that the maximum twin volume fraction increases at the initial stage and tends to be saturated at the late stage. Combining the results of simulations and neutron diffractions, the corresponding reasons are explained. Afterward, the mechanisms of the cyclic-hardening behavior at tension stage and compression stage are revisited, and some new insights are provided.

Small Crack Initiation and Early Propagation in an As-Extruded Mg-10Gd-3Y-0.5Zr Alloy in High Cycle Fatigue Regime

Small fatigue crack growth in an extruded dual-phase Mg-Li alloy

Localized dislocation interactions within slip bands and crack initiation in Mg-10Gd-3Y-0.3Zr alloy

Effect of basal texture on small crack behavior of magnesium alloy in very high cycle fatigue regime

Very high cycle fatigue resistance improvement of Mg-Gd-Zn-Zr alloy by introducing curved long-period stacking ordered lamellae

Quantitative assessment of the microstructural factors controlling the fatigue crack initiation mechanisms in AZ31 Mg alloy

Crack initiation and propagation characteristics of a dual‐phase Mg–Li alloy under high‐cycle and very‐high‐cycle fatigue regimes

Effect of microstructure and local stress on small crack initiation and propagation paths in coarse‐grained FeCrAl alloys

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Effect of long-period stacking ordered structure on very high cycle fatigue properties of Mg-Gd-Y-Zn-Zr alloys

Quantitative Investigation on the Slip/Twinning Activity and Cracking Behavior During Low-Cycle Fatigue of an Extruded Mg-3Y Sheet

Microstructure sensitivity of the low cycle fatigue crack initiation mechanisms for the Al 0.3 CoCrFeNi high entropy alloy: in-situ SEM study and crystal plasticity simulation

Low-cycle Fatigue Small Crack Initiation and Propagation Behaviour of Cast Magnesium Alloys Based on In-Situ SEM Observations

Initiation of internal fatigue crack in a carbide-free bainitic steel during high cycle fatigue

Crack initiation mechanisms of micro-textured Ti60 alloys with different dwell sensitivities subjected to fatigue and dwell fatigue loading

Fatigue crack propagation within Al-Cu-Mg single crystals based on crystal plasticity and XFEM combined with cohesive zone model

Damage evolution of extruded magnesium alloy from deformation twinning and dislocation slipping in uniaxial stress-controlled low cycle fatigue

In-situ synchrotron X-ray tomography investigation of damage mechanism of an extruded magnesium alloy in uniaxial low-cycle fatigue with ratchetting

Relationship Between the Fatigue Behavior and Grain Structures of an As-Extruded Mg-6.2%Zn-0.6%Zr (in Wt.%) Alloy

Microstructure related failure mechanism of selective laser melted GH4169 with interior fatigue cracking

Crystal plasticity modeling of low-cycle fatigue behavior of an Mg-3Al-1Zn alloy based on a model, including twinning and detwinning mechanisms