Abstract:Novel graphitizable pitches with controllable softening points and methylene-bridged structures were successfully prepared through photobromination of 1-methylnaphthalene (1-MNa) followed by closed-system dehydrobromination (CSD). The structures of bromination products and dehydrobromination pitches were determined using gas chromatography mass spectroscopy, NMR and laser desorption/ionization-time of flight/mass spectroscopy. It was found that the amount of bromine introduced greatly affected the composition of bromination products. 1-MNa brominated at a bromine/1-MNa molar ratio of 0.75 (BMNa-0.75) demonstrated the highest methyl bromination selectivity (S-mb), which was selected as the dehydrobromination precursor. After a CSD/polymerization reaction under 200-250 degrees C, dehydrobromination pitches with softening points of 148-226 degrees C were acquired. Compared with open-system dehydrobromination (OSD), CSD endowed bromine radical longer life and boosted intramolecular and intermolecular linking, thereby substantially increasing softening points and coking values. The polymerization degree of CSD-derived pitches is highly regulable depending on dehydrobromination temperature and the amount of tetrahydronaphthalene (tetralin) introduced. Moreover, methyl migration products (naphthalene, 2-methylnaphthalene, dimethyl-naphthalene and trimethyl-naphthalene) together with hydrogenation products (mainly tetralin) were detected by analyzing the hexane-soluble components (HS). The structural features of CSD, derived pitches contributed to some unique properties such as high polymerization degree accompanied by low aromaticity, continuous molecular weight distribution and complex connection types among subunits including alpha-alpha', alpha-beta', and beta-beta'. The semicoke with 94% anisotropy of coarse flow texture was synthesized at 420 degrees C under atmospheric pressure. Well-developed graphitic carbons with graphitization degree of 81.40% and I-D/I-G of 0.12 was obtained from graphitization of dehydrobromination pitches under 2600 degrees C.

Controllable Synthesis of Highly Graphitizable Pitches from 1-Methylnaphthalene Via Closed-System Dehydrobromination

Controllable synthesis of a carbonaceous pitch from molecular dimension by a novel method of chlorination-dechlorination

Controllable Preparation of Spinnable Isotropic Pitches for Carbon Fibers with High Tensile Strength from Low-Cost Ethylene Tar Pitch by a Selective Photobromination–debromination Method

Effects of Bromination-Dehydrobromination on the Microstructure of Isotropic Pitch Precursors for Carbon Fibers

Controllable synthesis of isotropic pitch precursor for general purpose carbon fiber using waste ethylene tar via bromination–dehydrobromination

Preparation of Mesophase Pitch with Fine-Flow Texture from Ethylene Tar/Naphthalene by Catalytic Synthesis for High-Thermal-Conductivity Carbon Fibers

Synthesis and Structural Evolution of Coal-Based Mesophase Pitch by Hydrogenation-Vacuum Thermal Polycondensation Process

Spinnable Mesophase Pitch Prepared via Co-carbonization of Fluid Catalytic Cracking Decant Oil and Synthetic Naphthalene Pitch

Preparation of pitch precursor with excellent spinnability for general-purpose carbon fibre using coal tar pitch as raw material

Chlorination–dechlorination of coal liquefaction residue using benzyl chloride for general-purpose carbon fiber synthesis

Reformation of Naphtha Cracking Bottom Oil for the Preparation of Carbon Fiber Precursor Pitch

Constructing the Bridge from Isotropic to Anisotropic Pitches for Preparing Pitch-Based Carbon Fibers with Tunable Structures and Properties

Mesophase pitch raw material used for preparing high-modulus high-thermal-conductivity carbon fiber, and preparation method thereof

Polymerization kinetics and control of the components of a mesophase pitch

Influence of boron trifluoride complex addition on structure and composition of mesophase pitch from FCC decant oil via two-stage thermotreatment

Mechanism and application of halogenation–dehalogenation in the development of pitch-based carbon fiber: A review

Tuning the carbon morphology by pyrolysis in AlCl3–NaCl molten salt from coal tar pitch

Preparation and characterization of pitch coke from oxidized polymerized pitch

Co‐Carbonization of Medium‐ and Low‐Temperature Coal Tar Pitch and Coal‐Based Hydrogenated Diesel Oil Prepare Mesophase Pitch for Needle Coke Precursor

Optimizing Aromaticity for Graphitization

Mechanism of coal pitch pre-hydrogenation catalyzed by metal-free catalytic system and preparation of mesophase pitch