High Temperature Oxidation Behavior of ZrB2-SiC Added MoSi2 Ceramics

Zongwei Tong,Rujie He,Tianbao Cheng,Keqiang Zhang,Dawei Dai,Yazheng Yang,Daining Fang
DOI: https://doi.org/10.1016/j.ceramint.2018.08.144
IF: 5.532
2018-01-01
Ceramics International
Abstract:In this paper, MoSi2, MoSi2-20 vol% (ZrB2-20 vol% SiC) and MoSi2-40 vol% (ZrB2-20 vol% SiC) ceramics were prepared using pressureless sintering. The oxidation behaviors of these MoSi2-(ZrB2-SiC) ceramics were investigated at 1600 degrees C for different soaking time of 60, 180 and 300 min, respectively. The oxidation behaviors of the MoSi2-(ZrB2-SiC) ceramics were studied through weight change test, oxide layer thickness measurement, and microstructure analysis. Further investigation of the oxidation behaviors of the MoSi2-(ZrB2-SiC) ceramics was conducted at a higher temperature of 1800 degrees C for 10 min. The microstructure evolution of the ceramics was also analyzed. It was finally found that the oxidation resistance of MoSi2 was improved by adding ZrB2-SiC additives, and the MoSi2-20 vol% (ZrB2-20 vol% SiC) ceramic exhibited the optimal oxidation resistance behavior at elevated temperatures. From this study, it is believe that it can give some fundamental understanding and promote the engineering application of MoSi2-based ceramics at high temperatures.
What problem does this paper attempt to address?