Abstract:Because CrAlN coating has excellent oxidation resistance components， it is widely used in the field of cutting tool coating. However， the thermal dcomposition of CrAlN coating above 900 ℃ leads to a drop in mechanical properties.Therefore， B and Si doping method was adopted in this study to further improve the performance of CrAlN coating. The structure， hardness， cohesion， thermal and machining properties of Cr 0.42 Al 0.58 N， Cr 0.35 Al 0.59 B 0.06 N and Cr 0.37 Al 0.54 Si 0.09 N deposited by cathodic arc evaporation are investigated by X-ray diffraction （XRD）， Scanning electron microscopy （SEM）， nano-indentation， scratch test and cutting experiment. The Cr 0.42 Al 0.58 N and Cr 0.37 Al 0.54 Si 0.09 N coatings present a single phase cubic structure， whereas the Cr 0.35 Al 0.59 B 0.06 N coating is mixed cubic-wurtzite structure. Cr 0.42 Al 0.58 N coating presents typical columnar crystal morphology along the growth direction. The addition of B and Si inhibits the growth of columnar crystals. The fracture morphology of Cr 0.35 Al 0.59 B 0.06 N coating and Cr 0.37 Al 0.54 Si 0.09 N coating are fine columnar crystals and nanocrystals respectively. The solid solution strengthening and grain refinement caused by B and Si doping increased the hardness of the coating from 29.8±1.5 GPa of Cr 0.42 Al 0.58 N coating to 36.9±1.4 GPa of Cr 0.35 Al 0.59 B 0.06 N coating and 33.8±1.6 GPa of Cr 0.37 Al 0.54 Si 0.09 N coating. However， B and Si doping reduced the cohesion with substrate from 116.2 N of Cr 0.42 Al 0.58 N coating to 58.3 N and 58.0 N of Cr 0.35 Al 0.59 B 0.06 N and Cr 0.37 Al 0.54 Si 0.09 N. The grain refinement caused by the addition of B and Si reduces the elastic modulus of the coating. The elastic modulus of Cr 0.42 Al 0.58 N， Cr 0.35 Al 0.59 B 0.06 N and Cr 0.37 Al 0.54 Si 0.09 N coatings are 523.6， 484.8 and 431.7 GPa respectively. The addition of B and Si improves the plastic deformation resistance of the coating. The ratios of H 3 /E 2 of Cr 0.42 Al 0.58 N， Cr 0.35 Al 0.59 B 0.06 N and Cr 0.37 Al 0.54 Si 0.09 N coatings are 0.097， 0.213 and 0.206 respectively. The addition of B and Si inhibits the fracture of Cr-N bond， thus retards the thermal decomposition process. The initial fracture temperature of Cr-N bond increased from 1000 ℃ of Cr 0.42 Al 0.58 N to 1200 ℃ of Cr 0.35 Al 0.59 B 0.06 N and 1100 ℃ of Cr 0.37 Al 0.54 Si 0.09 N. In addition， the formation temperature of w-AlN is increased from 1000℃ of Cr 0.42 Al 0.58 N to 1100 ℃ of Cr 0.35 Al 0.59 B 0.06 N. The doping of B and Si promoted the formation of dense oxides on the surface of the coating during oxidation， thus significantly improving the high-temperature oxidation resistance of the coating. After oxidation at 1100 ℃ for 15 h， the oxide layer thickness of Cr 0.42 Al 0.58 N and Cr 0.35 Al 0.59 B 0.06 N coatings is 2.38 μm and 1.80 μm. Cr 0.37 Al 0.54 Si 0.09 N coating shows the best oxidation resistance， and the thickness of the oxide layer of the coating is only 0.53 μm. A mixed oxide layer consisting of Al 2 O 3 ， Cr 2 O 3 and SiO 2 is grown on the surface of the coating containing Si. The oxide layer can avoid the formation of porous structure， thus maintaining a good combination with the residual nitride layer and providing effective protection for the coating.B and Si doping can improve the cutting performance of CrAlN coating on titanium alloy materials， After 45 min of cutting， the wear amount of Cr 0.42 Al 0.58 N， Cr 0.35 Al 0.59 B 0.06 N and Cr 0.37 Al 0.54 Si 0.09 N coated inserts is 0.5 mm， 0.071 mm and 0.173 mm respectively.

Structural, Mechanical and Thermal Properties of CrAlNbN Coatings

Structure, Mechanical Properties, Thermal Stability and Oxidation Resistance of Arc Evaporated CrAlBN Coatings

Thermal Stability and Oxidation Resistance of Cr1−xAlxN Coatings with Single Phase Cubic Structure

Effects of B and Si Doping on CrAlN Coating Structure and Tool Life of Cutting Titanium Alloy

Influence of TiN and ZrN Insertion Layers on the Microstructure, Mechanical and Thermal Properties of Cr–Al–N Coatings

Effect of CrN Addition on the Structure, Mechanical and Thermal Properties of Ti-Al-N Coating

Improvement of the Mechanical, Tribological Properties and Oxidation Resistance of AlCrVN Coatings by Nb Alloying

Thermal and Thermo-Mechanical Properties of Ti–Al–N and Cr–Al–N Coatings

Influence of Zr on Structure, Mechanical and Thermal Properties of Cr–Al–N Coatings

Structure, mechanical and thermal properties of CrAlBSiN coatings prepared by cathodic arc evaporation

Microstructures and initial oxidation of Nb-Cr based coating systems

Structure, Mechanical and Thermal Properties of Y-doped CrAlN Coatings

Improvement of Tribological Performance of TiAlNbN Hard Coatings by Adding AlCrN

Effect of V-addition on the Thermal Stability and Oxidation Resistance of CrAlN Coatings

Structure and Thermal Properties of TiAlN/CrN Multilayered Coatings with Various Modulation Ratios

Structure and Property Optimization of Ni-containing AlCrSiN Coatings by Nano-Multilayer Construction

Microstructure, mechanical properties, and oxidation behavior of arc-evaporated Cr–Al–O–N coatings with various Cr/Al ratios

Influence of Interlayer Materials on the Mechanical Properties and Thermal Stability of a CrAlN Coating on a Tungsten Carbide Substrate

Influence of Ni-addition on Mechanical, Tribological Properties and Oxidation Resistance of AlCrSiN Coatings

Influence of Oxygen Addition on the Structure, Mechanical and Thermal Properties of CrN Coating

Microstructures, Mechanical Properties and Tribological Behaviors of NiAl-based Composite Coatings with Various Addition of Nb