Abstract:SiC ceramic samples were brazed to each other in air using ultrasonic-assisted brazing, filling with ZnAlMg alloys at 420°C. The microstructure, mechanical properties, and interfacial bonding mechanism of the joint were investigated. The ultrasonic vibration duration time (UVDT) significantly affected the strength of the joint. A joint with a high strength of ∼148MPa was obtained when the UVDT was increased to 8s. An amorphous SiO2 film with a thickness of ∼6nm was formed on the surface of SiC during heating in air. When ultrasonically vibrated, the liquid ZnAlMg filler metal eroded the SiO2 film nonuniformly. This erosion behavior was induced by the impact from liquid micro-jets, shock waves, and localized high temperatures, all of these effects being ascribed to the implosion of the cavitation bubble. The atoms generated from the erosion of the SiO2 film diffused away quickly in the liquid alloy, aided by the acoustic streaming effect. This erosion behavior belonged to a special phenomenon of cavitation erosion. Other amorphous phases not eroded by the liquid ZnAlMg alloy were preserved at the final interface. Strong bonding between the SiC and the ZnAlMg filler metal could be ascribed to cavitation erosion-induced mass transfer from SiO2 to ZnAlMg; this mass transfer behavior was enhanced by prolonging the UVDT.

Application of a New Ultrasonic-Assisted Semi-Solid Brazing on Dissimilar Al/Mg Alloys

Reduction of Intermetallic Compounds in Ultrasonic-Assisted Semi-Solid Brazing of Al/Mg Alloys

Ultrasonic-Assisted Semi-Solid Forming Method and Microstructure Evolution of Aluminum/Copper Brazed Joints

Ultrasound-assisted Brazing of Cu/Al Dissimilar Metals Using a Zn–3Al Filler Metal

Interfacial Microstructure and Mechanical Properties of Ultrasonic-Assisted Brazing Joints Between Ti–6Al–4V and ZrO2

Interfacial reaction of intermetallic compounds of ultrasonic-assisted brazed joints between dissimilar alloys of Ti-6Al-4V and Al-4Cu-1Mg

Microstructure and Mechanical Properties of Ultrasonically Assisted Brazing of Dissimilar Cu–Al Alloys

Interaction Behaviors at the Interface Between Liquid Al–Si and Solid Ti–6Al–4V in Ultrasonic-Assisted Brazing in Air

Ultrasonic-assisted fluxless reactive bonding of Mg/Al dissimilar alloy using Zn–Al solder in air

Ultrasonic-assisted Brazing of Al–Ti Dissimilar Alloy by a Filler Metal with a Large Semi-Solid Temperature Range

Microstructure and Mechanical Properties of Ti–6Al–4V/Al1060 Joints by Ultrasonic-Assisted Brazing in Air

Ultrasonic-assisted brazing of sapphire with high strength Al–4.5Cu–1.5Mg alloy

Ultrasonic-assisted liquid–solid composite method to fabricate bimetallic aluminum alloy

Control Al/Mg Intermetallic Compound Formation During Ultrasonic-Assisted Soldering Mg to Al.

Microstructure, Mechanical Properties, and Bonding Mechanism of Ultrasonic-Assisted Brazed Joints of Sic Ceramics with Znalmg Filler Metals in Air

Microstructure and Strength of Ultrasonic-Assisted Brazed Joints of Si3N4/6061Al Composites

Formation of Amorphous Interfacial Layer Between Zn-based Alloy and SiC Particles under Ultrasonic-Assisted Brazing

Ultrasonic-assisted brazing of Al/Fe with Al alloy

Microstructures and Properties of Alumina/copper Joints Fabricated by Ultrasonic-Assisted Brazing for Replacing DBC in Power Electronics Packaging

Joint formation and mechanical properties of ultrasonic-assisted transient liquid bonding of dissimilar Al/Mg with a Zn interlayer in air

Effect of Ultrasonic Transmission Rate on Microstructure and Properties of the Ultrasonic-Assisted Brazing of Cu to Alumina.