Abstract:SiC ceramic samples were brazed to each other in air using ultrasonic-assisted brazing, filling with ZnAlMg alloys at 420°C. The microstructure, mechanical properties, and interfacial bonding mechanism of the joint were investigated. The ultrasonic vibration duration time (UVDT) significantly affected the strength of the joint. A joint with a high strength of ∼148MPa was obtained when the UVDT was increased to 8s. An amorphous SiO2 film with a thickness of ∼6nm was formed on the surface of SiC during heating in air. When ultrasonically vibrated, the liquid ZnAlMg filler metal eroded the SiO2 film nonuniformly. This erosion behavior was induced by the impact from liquid micro-jets, shock waves, and localized high temperatures, all of these effects being ascribed to the implosion of the cavitation bubble. The atoms generated from the erosion of the SiO2 film diffused away quickly in the liquid alloy, aided by the acoustic streaming effect. This erosion behavior belonged to a special phenomenon of cavitation erosion. Other amorphous phases not eroded by the liquid ZnAlMg alloy were preserved at the final interface. Strong bonding between the SiC and the ZnAlMg filler metal could be ascribed to cavitation erosion-induced mass transfer from SiO2 to ZnAlMg; this mass transfer behavior was enhanced by prolonging the UVDT.

Microstructure and Strength of Ultrasonic-Assisted Brazed Joints of Si3N4/6061Al Composites

Microstructure and Mechanical Properties of Ti–6Al–4V/Al1060 Joints by Ultrasonic-Assisted Brazing in Air

Interfacial Microstructure and Mechanical Properties of Ultrasonic-Assisted Brazing Joints Between Ti–6Al–4V and ZrO2

Microstructure, Mechanical Properties, and Bonding Mechanism of Ultrasonic-Assisted Brazed Joints of Sic Ceramics with Znalmg Filler Metals in Air

Ultrasonically Aided Brazing of SiCp/A356 Composites

Microstructure and Joint Properties of Ultrasonically Brazed Al Alloy Joints Using a Zn–Al Hypereutectic Filler Metal

Si Particulate-Reinforced ZnAl Based Composites Joints of Hypereutectic Al50Si Alloys by Ultrasonic-Assisted Soldering

Microstructure and Mechanical Properties of Ultrasonically Assisted Brazing of Dissimilar Cu–Al Alloys

Microstructure and properties of the Si3N4/Si3N4 brazing joint

Ultrasonic brazing of high fraction volume of SiC particulate reinforced aluminium matrix composites

Research on the Interfacial Structure and Properties of TiAl - Si3N4f/Si3N4 Brazed Joints

Interfacial microstructure and mechanical properties of porous-Si3N4 ceramic and TiAl alloy joints vacuum brazed with AgCu filler

Ultrasound-assisted Brazing of Cu/Al Dissimilar Metals Using a Zn–3Al Filler Metal

Interfacial Structure and Formation Mechanism of Ultrasonic-Assisted Brazed Joint of Sic Ceramics with Al-12si Filler Metals in Air

Acoustic cavitation-induced microstructure evolution in ultrasonically brazed Al/Cu joints using Zn-Al alloy fillers

Ultrasonic brazing of SiC particulate reinforced aluminum matrix composites with high fraction volume

Ultrasonic Dissolution of Brazing of 55% SiCp/A356 Composites

Formation of Amorphous Interfacial Layer Between Zn-based Alloy and SiC Particles under Ultrasonic-Assisted Brazing

Ultrasonic-assisted brazing of Al/Fe with Al alloy

Microstructure and Mechanical Properties of Ultrasound-Assisted Soldered Al-50 Wt.%si/al-27 Wt.%si Joints for Automotive Applications

Strengthening Mechanism of Ceramic Particle Reinforced Bonds by Ultrasonic Brazing of AlMMCs