LiYGeO4: Novel Low-Permittivity Microwave Dielectric Ceramics with Intrinsic Low Sintering Temperature

Kai Cheng,Chunchun Li,Huaicheng Xiang,Yihua Sun,Liang Fang

DOI: https://doi.org/10.1016/j.matlet.2018.05.124

IF: 3

2018-01-01

Materials Letters

Abstract:Using the solid-state reaction route, a new low-firing microwave dielectric ceramic LiYGeO4 was prepared, and the phase evolution, thermal stability, and dielectric properties were characterized. A single orthorhombic phase LiYGeO4 formed in the sintering temperature range of 920-960 degrees C decomposed into Y2GeO5,GeO2, and Li2O when the sintering temperature exceeded 960 degrees C. LiYGeO4 densified at 940 degrees C/6 h possessed a relative permittivity 9.41, a quality factor 18,860 GHz (at 12.8 GHz), and a temperature coefficient of resonant frequency -27.7 ppm/degrees C. The negative tau(f) value was compensated by compositing with CaTiO3, and 0.97LiYGeO(4)-0.03CaTiO(3) ceramic exhibited a near-zero tau(f) of -1.37 ppm/degrees C along with a permittivity of 9.83 and a quality factor of 12,940 GHz (at 13.2 GHz). All merits make LiYGeO4 a promising candidate for high-frequency communication application, and low-temperature co-fired ceramics. (C) 2018 Elsevier B.V. All rights reserved.