Densification, microwave dielectric properties and rattling effect of LiYbO2 ceramics with low εr and anomalous positive τf

Jiangyu Zhang,Jie Li,Yihua Sun,Liang Fang

DOI: https://doi.org/10.1016/j.jeurceramsoc.2022.09.010

IF: 5.7

2022-12-01

Journal of the European Ceramic Society

Abstract:LiYbO2 ceramic with tetragonal structure formed only by [LiO6] and [YbO6] octahedra, exhibited a εr of 13.3 ± 0.2, Q × f of 24,700 ± 500 GHz and an abnormal positive τf of + 38.6 ± 3.0 ppm/°C as sintered at 1100 °C with low relative density of 88 %. Dense ceramic with relative density of 95.1 % was obtained with the addition of 1 wt% LiF when sintered at 1080 °C, exhibiting enhanced microwave dielectric properties of εr = 14.3 ± 0.2, Q × f = 41,200 ± 500 GHz, τf = +56.5 ± 3.0 ppm/°C and αL = 8.5 × 10−6/K. The large positive discrepancy as much as + 45.1 % between measured εr with porosity correction and calculated εr(C-M) using Clausius−Mossotti relations might be due to the rattling effect of Li+, which also led to the positive τf.

materials science, ceramics