Microwave dielectric properties and chemical bond characteristics of low temperature firing Li3VO4 ceramic with low permittivity

Ching-Fang Tseng,Wen-Hung Chang,Bo-Zhong Huang,Chen-Hung Han

DOI: https://doi.org/10.1016/j.ceramint.2023.08.312

IF: 5.532

2023-09-01

Ceramics International

Abstract:Low-fired Li3VO4 ceramics were fabricated and their sintering characteristics, intrinsic structure of the crystal, and microwave dielectric performances were discussed. After the Rietveld refinements, all samples showed the single orthorhombic Li3VO4 phase with the space group Pnm21 over the sintering temperature 700–820 °C for 2–6 h. The results presented that the permittivity, quality factor, and density exhibited a close correlation at different sintering conditions. The homogenous microstructures and outstanding dielectric performances were achieved upon sintering at 730 °C/4h: ε r of 6.65, Q × f value of 15,700 GHz, and τ f of −103 ppm/°C. The intrinsic characteristics of Li3VO4 compounds were also discussed by chemical bond theory. The results indicated that the V(1)–O bonds dominated the contribution to the dielectric properties of the Li3VO4 ceramics.

materials science, ceramics