Abstract:It is known that welded joint is much “weaker” than base metal due to discontinuities of geometry, materials and residual stresses. It seems current international design rules do not adopt a uniform approach to weld efficiency, which is often defined as the ratio of the strength of a welded joint to the strength of base metal, in their guidance for creep and fatigue design of welds. This appears to be a great barrier for the application of nuclear welded structures which has a prolonged design lifetime of 60 years. In this work, fatigue strength reduction factor of a Cr-Ni-Mo-V steel welded joint, machined from welded steam turbine rotors for nuclear power plant, was investigated by performing axially push-pull cyclic loads tests with both cross-weld and pure base metal specimens up to very high cycle fatigue regime under ultrasonic frequency at ambient temperature. The effects of residual stress, strain localization, and microdefects in mismatched steels on failure mechanisms of welds were discussed thoroughly. Results show that fatigue strength reduction factor is varied in the range of 0.95-0.975, and is found to be dependent on fatigue lifetime for the first time. It is indicated that variation of fatigue strength reduction factor are associated with transition of crack initiation from specimen surface in high cycle fatigue regime to interior micro-defects in very high cycle fatigue regime. Comparing existing codes and standards for fatigue design of welds with experimental data indicates the over-conservativeness of present code-based design method. This implies a micro-defect based fatigue design approach is required for long life safe and reliability of weldments.

Failure Mechanisms and Design of Dissimilar Welds of 9%cr and CrMoV Steels Up to Very High Cycle Fatigue Regime

Low Cycle Fatigue Properties and Fracture Mechanism of Q345qC Steel and Its Welded Joint

Failure Mechanisms and Fatigue Strength Reduction Factor of a Cr-Ni-Mo-V Steel Welded Joint Up to Ultra-Long Life Regime

Low-Cycle Fatigue Behavior of 10crni3mov High Strength Steel and Its Undermatched Welds

Very High Cycle Fatigue Behavior of 25cr2ni2mov Steel Welded Joint

Microstructure Correlation and Fatigue Crack Growth Behavior in Dissimilar 9cr/crmov Welded Joint

Effect of Carbon Migration on Interface Fatigue Crack Growth Behavior in 9cr/crmov Dissimilar Welded Joint

Low Cycle Fatigue Properties of a 9–12% Cr Martensitic Steel Welded Joint with Ni-based Weld Metal Based on a Local Strain Approach

On Specimen Design for High Cycle Fatigue Testing of Welded Joint

Microstructure Characterization and HCF Fracture Mode Transition for Modified 9Cr-1Mo Dissimilarly Welded Joint at Different Elevated Temperatures

Microstructural Characteristics and Low Cycle Fatigue Properties at 230 °C of Different Weld Zone Materials from a 100 Mm Thick Dissimilar Weld of Ultra-Supercritical Rotor Steel

Very High Cycle Fatigue Behavior And Life Prediction Of A Low Strength Weld Metal At Moderate Temperature

A Comparative Study on the Cyclic Plasticity and Fatigue Failure Behavior of Different Subzones in CrNiMoV Steel Welded Joint

Effect of Temperature on High‐cycle Fatigue and Very High Cycle Fatigue Behaviours of a Low‐strength Cr–Ni–Mo–V Steel Welded Joint

Understanding of Fatigue Crack Growth Behavior in Welded Joint of a New Generation Ni-Cr-Mo-V High Strength Steel

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Fatigue crack growth behavior of Ni-Cr-Mo-V steel welded joints considering strength mismatch effect

Fatigue Crack Growth Rates of 10crni3mov Steel Welded Joints Considering the Stress Ratio

Two Fatigue Fracture Modes at Different Temperatures of 10%cr Heat-Resistant Steel Weldment Filled with Ni-Based Alloy

Some issues of fatigue failure of welded structures

Failure mechanisms and fatigue strength assessment of a low strength Cr−Ni−Mo−V steel welded joint: Coupled frequency and size effects