Abstract:This work investigates the heterogeneous deformation and failure of HR3C austenitic stainless steel welded joints at room and typical service temperatures. Such types of welded joints are widely used in the new generation of fossil fuel power stations and are known to suffer from premature high temperature failure. Observation of in-service failures revealed that cracks may nucleate either in the heat affected zone or in the weld metal. The main objective of this work is to identify the local microstructural conditions and stress–strain fields responsible for both ductile failure and micro-crack nucleation within the weldment at low and high temperatures, respectively. To that purpose, a novel multi-scale micromechanics-based modelling framework is proposed. It relies on representative weld microstructure models digitally reconstructed from EBSD measurements, and dislocation density-based crystal plasticity models to describe the behaviour of individual grains in each weld region. A novel thermo-dynamically consistent relation for the configuration stored energy per unit volume is derived from the crystal plasticity framework. The single crystal models are calibrated and validated from a combination of uniaxial tensile tests on cross-weld specimens using high resolution digital image correlation techniques, representative volume elements of the polycrystals at the macro-scale, as well as micropillar compression tests at the scale of the individual grains. Predictions of heterogeneous inelastic deformation fields within the weldment at both 22 °C and 665 °C, and of micropillar compression behaviour of the individual weld single crystal phases are consistent with experimental data. The experimentally observed ductile failure of the weld metal at room temperature is successfully predicted using a Gurson-type void nucleation, growth and coalescence constitutive model. The suitability of the stored strain energy density and the accumulated plastic strain as crack initiation/creep failure indicators is investigated. It was found that predicted creep lifetimes with either indicator were very similar, and that they were relatively accurate for low stress levels.

Role of nano-sized precipitates on LCF failure behavior for the CrMoV steel welded joint after long-term high temperature service

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Low Cycle Fatigue and Creep Fatigue Interaction Behavior of 9Cr-0.5Mo-1.8w-v-nb Heat-Resistant Steel at High Temperature

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Influence of Prior Low Cycle Fatigue on Microstructure Evolution and Subsequent Creep Behavior

Characterization of Low Cycle Fatigue Performance of New Ferritic P92 Steel at High Temperature: Effect of Strain Amplitude

Low cycle fatigue and creep-fatigue interaction behavior of 2.25CrMoV steel at high temperature

Near-threshold Fatigue Crack Growth Behavior of the Weld Metal and Heat-Affected Zone in an Ex-Service CrMoV Steel Joint

Effect of long-term aging on the low cycle fatigue behavior and microstructure of a 10% Cr martensitic steel with low nitrogen and high boron contents at 650 °C

Study on Low‐Cycle Fatigue Behavior and Life Prediction of Cr–Ni–Mo–V Gun Steel at Room Temperature and 600 °C

A comparative study of low cycle fatigue behavior and microstructure of Cr-based steel at room and high temperatures

Evolution and Coarsening of Carbides in 2.25Cr-Lmo Steel Weld Metal During High Temperature Tempering

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

Effect of stress on the nucleation and evolution of Mo-rich Laves phase in 9.5Cr-1.5MoCoVNbNB heat-resistant steel during tensile rupture at 620 °C

Effects of temperature and strain amplitude on low-cycle fatigue behavior of 12Cr13 martensitic stainless steel

Low-cycle fatigue of MCrAlY-coated superalloys: a fracture mechanics-based analysis

Evolution mechanism of interfacial microstructure and its effect on failure in dissimilar metal welds containing ferritic heat resistant steels

The Effect of Microstructure on the Fatigue Crack Growth Behavior of Ni-Cr-Mo-V Steel Weld Metal

Stabilities of the precipitates in CLAM steel during 30,000 h thermal aging

Thermal evolution and strengthening mechanisms in LPBF CoCrFeMnNi alloy: New insights on correlation between microstructure and mechanics with LAGBs

Low cycle fatigue behavior of 316LN stainless steel: Effects of temperature, strain rate and strain amplitude