Abstract:This research has demonstrated that SiO 2 impregnation under high vacuum pressure of − 90 kPa can significantly reduce porosity by almost 10%, and improve the mechanical and viscoelastic properties of spruce wood under dry and saturated states. Characterization methods, such as impact test, DMA, SEM, EDS, porosity and SAXS tests were conducted on non-treated and − 90 kPa treated spruce wood samples under dry, saturated and submerged states to analyze the synergistic effect of high vacuum SiO 2 impregnation pressure on wood properties. The results showed that high vacuum impregnation pressure had a significant positive reinforcing effect on wood's properties. It increased the impact resistance of wood under dry and saturated conditions. Additionally, the high vacuum impregnation technique was able to overcome the water-induced softening effect and caused a significant increase in the storage modulus through uniform dispersion of the SiO 2 particles in the wood's vascular structure. Consequently, the impregnation reinforced the wood and ameliorated its capacity to absorb energy. High vacuum impregnation was also able to counteract the plasticizing effect of the water molecules and significantly increased the loss modulus by increasing the internal friction and cohesion of the wood components with the addition of the nanoparticles to the vascular system, which increased the wood's capacity to transform and dissipate energy. Quantitatively and qualitatively, impregnation under a vacuum pressure of − 90 kPa exhibited an effective obstruction of the vascular structure of spruce wood. In all conditions, high vacuum-impregnated samples showed significant enhancements over non-treated samples. This research demonstrated that high vacuum SiO 2 impregnation is an effective wood processing technique. Multiple materials and applications could benefit from this research wherein high strain-rate deformations are expected to occur or when simultaneous elastic behaviour of wood and its damping energy is needed. This study could also pave the way for research on the synergistic effect of SiO 2 impregnation and water absorption on the viscoelastic behaviour of wood.

Recovery of Thermally Compressed Scots Pine (pinus Sylvestris L.) Wood

Analysis of Deformation Fixation of Thermally Compressed Scots Pine (pinus Sylvestris L.)

Delayed Elastic Strain and Set-Recovery Evaluation in High-Pressure Densified Hybrid Poplar Wood – New Assessment Considerations

High-Pressure Treatment of Chinese Fir Wood: Effect on Density, Mechanical Properties, Humidity-Related Moisture Migration, and Dimensional Stability

Effect of High-pressure Densification on Moisture Sorption Properties of Paulownia Wood

Effects of High-Pressure Treatment on Poplar Wood: Density Profile, Mechanical Properties, Strength Potential Index, and Microstructure

Chemical Analysis of Densification, Drying, and Heat Treatment of Scots Pine (pinus Sylvestris L.) Through a Hot-Pressing Process

MOISTURE SORPTION ISOTHERMS AND ISOSTERIC HEATS OF SORPTION OF HIGH-PRESSURE TREATED PAULOWNIA WOOD UNDER DIFFERENT STORAGE CONDITIONS

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

Plastic and Elastic Strains in Poplar Wood under High-Pressure Densification

The study of physico-mechanical properties of SiO2-impregnated wood under dry and saturated conditions

Pore Analysis Of Thermally Compressed Scots Pine (Pinus Sylvestris L.) By Mercury Intrusion Porosimetry

Thermodynamic Property of Heat Treated and Compressed Larch and Poplar Wood

Surface densification and high temperature hydrothermal post treatment of the Abies nephrolepis lumber

How thermal treatment affects the chemical composition and the physical, mechanical and swelling properties of Scots pine juvenile and mature wood

Dynamic Thermo-Mechanical Analysis for the Compressive Rectangle Wood

Characterization of hygrothermal, gas pressure and stress characteristics for poplar wood during unilateral surface densification

Trinity Technology Optimization of Drying, Densifying and Charring of Pinus sylvestris

Densification of Delignified Wood: Influence of Chemical Composition on Wood Density, Compressive Strength, and Hardness of Eurasian Aspen and Scots Pine

Thermo-oxidative Decomposition and Combustion Behavior of Scots Pine (pinus Sylvestris L.) Sapwood Modified with Phenol- and Melamine-Formaldehyde Resins

Flame-retardant, Heat-Insulating and Char Formation Properties of Densified Pinus Sylvestris Treated with Different Compression Pressures