Abstract:Densified wood (DW) is a promising functional material with excellent mechanical performance, whose applications are restricted by fire safety problem. The key to solving this problem is to understand the effects of the components and density on wood thermal decomposition and combustion behaviors while keeping other influencing properties constant. In this study, natural wood (NW), lignin modified wood (MW) and DW were comparatively studied by thermogravimetric analysis (TGA) and cone calorimetry tests. MW was prepared by delignification process to reduce the hemicellulose and lignin contents, while DW was obtained by further densification treatment which increased wood density. TGA pyrolysis showed that MW and DW presented enhanced thermal stability as they had a 7% increase in char yield and decreased peak mass loss rates. A 0D numerical model including four parallel reactions was employed to simulate the pyrolysis behaviors. Particle swarm optimization algorithm was applied to exact the pyrolysis kinetics and stoichiometric coefficients. Two different sets of kinetics were obtained for NW and MW (or DW) since the delignification changed the pyrolysis evolutions. The model predictions well agreed with the measurements for all wood samples. Results from cone calorimetry tests showed that both delignification and densification delayed ignition time. DW formed a compact char layer, which slowed the heat release rate (HRR) decline after the second HRR peak. Wood component contents and density had negligible impacts on characteristic HRR and heat of combustion. Analytical study was performed to obtain thermal inertia and critical heat flux. NW and MW were treated as thermally thin material, while DW spanned the thermally intermediate and thick regimes. DW had the highest thermal inertia due to its dense structure. The critical heat flux of DW and MW were close and higher than that of NW, which could be explained by their increased thermal stability.

Thermo-oxidative Decomposition and Combustion Behavior of Scots Pine (pinus Sylvestris L.) Sapwood Modified with Phenol- and Melamine-Formaldehyde Resins

Fire resistance of pine wood treated with phenol-formaldehyde resin and phosphate-based flame retardant

Resistance against fungal decay of Scots pine sapwood modified with phenol-formaldehyde resins with substitution of phenol by lignin pyrolysis products

Comparative studies on the durability and moisture performance of wood modified with cyclic N-methylol and N-methyl compounds

Thermal Decomposition of Wood Treated with K<sub>2</sub>CO<sub>3</sub> and Melamine Modified Phenolic Resin by Thermogravimetry–Mass Spectrometry

Effects of the combination of phenolic-resin impregnation and heat treatment on physical, mechanical and decay resistance of Taxodium hybrid "Zhongshanshan" wood

Tensile and Impact Bending Properties of Chemically Modified Scots Pine

Phosphorylated and carbamylated Kraft lignin for improving fire- and biological-resistance of Scots pine wood

Comparative Study of Organic and Inorganic Modification of Chinese Fir Wood Based on the Respiratory Impregnation Method

Fire-retardant properties of wood modified with sorbitol, citric acid and a phosphorous-based system

Improvement in fire retardancy with double-step chemical modification on Pinus radiata D. Don using dimethyl methylphosphonate with propylene oxide and maleic anhydride

Combustion Behavior and Thermal Degradation Properties of Wood Impregnated with Intumescent Biomass Flame Retardants: Phytic Acid, Hydrolyzed Collagen, and Glycerol

High Leach-Resistant Fire-Retardant Modified Pine Wood (Pinus sylvestris L.) by In Situ Phosphorylation and Carbamylation

Wood modification with phenol urea formaldehyde (PUF) resin: the influence of wood species selection on the dimensional stability

Flame-retardant, Heat-Insulating and Char Formation Properties of Densified Pinus Sylvestris Treated with Different Compression Pressures

Construction of a Phytic Acid–Silica System in Wood for Highly Efficient Flame Retardancy and Smoke Suppression

A new wood-modification process based on in situ grafting of urethane groups: biological resistance and dimensional stability of carbamylated Scots pine wood

Changes in Physical Properties of Sugi, Hinoki, and Korean Pine Wood after Fire-retardant Treatment

In-Situ Synthesized Phosphorus–Boron–Magnesium Hybrid Flame Retardants with Core-Shell Structures in Wood Microstructures: an Effective Strategy for Realizing Durable Fire Retardancy, Smoke Suppression, and Anti-Degradation

Pyrolysis and Combustion Behaviors of Densified Wood

New Perspective on Wood Thermal Modification: Relevance between the Evolution of Chemical Structure and Physical-Mechanical Properties, and Online Analysis of Release of VOCs