Abstract:A flame retardant composition was prepared by using phosphoguanidine, guanidine sulfamate, disodium octaborate tetrahydrate and dodecyl dimethyl benzyl ammonium chloride. Veneers were immersed in such flame retardant mixture to prepare plywood. The combustion characteristics and thermal stability of plywood were assessed using a cone calorimeter and TG. Results showed that: (1) High concentration and loading of flame retardant were beneficial for the fire resistance of the plywood. (2) The limiting oxygen index (LOI) and residual mass of plywood processed using the flame retardant was increased by 87.52% and 58.66% compared to those of the untreated plywood, while the average heat release rate (av-HRR), total heat release (THR), effective heat of combustion (EHC), total smoke release (TSR), CO yield (COY), CO2 yield (CO2Y) and oxygen consumption were decreased by 44.3%, 82.9%, 47.0%, 86.0%, 89.9%, 50.1% and 83.1%, respectively. (3) Treated plywood which had a low fire growth index (FGI) displayed a later combustion heat release rate peak and slower flame spread than observed for the untreated material. Combustion of treated plywood displayed a higher fire performance index (FPI), indicating a longer time to ignition. This suggests that burning structures from this material would be subject to a longer time for escape from the structure and would present lower fire risk than similar structures containing treated plywood. (4) TG results demonstrated that the presence of the flame retardant can decrease the pyrolysis temperature for hemicellulose and cellulose, change the decomposition and reaction progress for plywood degradation and promote dehydration carbonization and accelerated charformation. Moreover, the formed char was more stable than that combustion of untreated plywood. (5) The flame retardant contains nitrogen (N), phosphorus (P), boron (B), chlorine (Cl) and guanidine (Gu) compounds. The adhesive also contains N and P compounds. These substances display flame resistance and supplement each other to generate flame retardance than any one used alone. By changing the thermolysis and thermal decomposition processes, the heat release and smoke release from plywood, undergoing combustion was reduced. This controlled generation of combustible substances and promoted dehydration and carbonization to form char. As a result, the flame resistance of plywood was improved significantly. The probability of smoke asphyxia or poisoning death of those trapped in structures containing treated plywood during fire accidents can be decreased dramatically.

Combustion Behavior and Thermal Degradation Properties of Wood Impregnated with Intumescent Biomass Flame Retardants: Phytic Acid, Hydrolyzed Collagen, and Glycerol

Construction of a Phytic Acid–Silica System in Wood for Highly Efficient Flame Retardancy and Smoke Suppression

Flame Retardancy of Densified Wood Modified by Bio-Material Based Flame Retardant

In-Situ Synthesized Phosphorus–Boron–Magnesium Hybrid Flame Retardants with Core-Shell Structures in Wood Microstructures: an Effective Strategy for Realizing Durable Fire Retardancy, Smoke Suppression, and Anti-Degradation

Study of Burning Behaviors and Fire Risk of Flame Retardant Plywood by Cone Calorimeter and TG Test

Infusing phytate-based biomass flame retardants into the cellulose lumens of Chinese fir wood attains superior flame retardant efficacy

Impregnation of phytic acid into the delignified wood to realize excellent flame retardant

Intumescent fire-retardant coatings for ancient wooden architectures with ideal electromagnetic interference shielding

In-situ incorporation of metal phytates for green and highly efficient flame-retardant wood with excellent smoke-suppression property

Modification with Lignin-Based N-P Flame Retardant to Improve the Flame Retardancy and Smoke Suppression of Wood

Influence Of Phytic Acid On Flame Retardancy And Adhesion Performance Enhancement Of Poly (Vinyl Alcohol) Hydrogel Coating To Wood Substrate

Phytate-based Transparent and Waterproof Intumescent Flame-Retardant Coating for Protection of Wood

A Fully Bio-Based Intumescent Flame Retardant for Enhancing the Flame Retardancy and Smoke Suppression Properties of Wood Flour Polypropylene Composites

The Combustion and Mechanical Properties of Guanidine Phosphate-Boron Compound-Silica Sol Composite Flame Retardant on Wooden Structure Building Components

Effect of a biomass based waterborne fire retardant coating on the flame retardancy for wood

Pyrolysis and Combustion Behavior of Pinewood after the Addition of Flame Retardants

Preparation of multifunctional flame-retardant and superhydrophobic composite wood by iron ions doped phytic acid-based nanosheets

Preparation of Organic-Inorganic Phosphorus-Nitrogen-Based Flame Retardants and Their Application to Plywood

Physical Chemistry of the Interaction of Cellulose with Lignin during Wood Surface Treatment with a Phosphate Flame Retardant

Effect of phosphorus/nitrogen/carbon component ratio in aqueous flame retardant on the fire prevention of wood substrate

Multifunctional Flame-Retardant, Thermal Insulation, and Antimicrobial Wood-Based Composites.