Abstract:<p>Carbon fibre-reinforced polymer (CFRP) plates are widely used to strengthen reinforced-concrete (RC) structures. At present, most studies focused on the short-term performance of strengthened RC beams with a prestressed CFRP plate, and very limited information is available on their durability, which is of importance in certain cases, such as high-piled wharfs and bridges in marine environments. This study investigates the effects of chloride environment exposure on the flexural performance of strengthened RC beams with self-anchored prestressed CFRP plates. In total, seven RC beams, four of which were strengthened by a self-anchored prestressed CFRP plate, were fabricated and tested under three-point bending. The testing parameters included 25% and 40% prestress level of the ultimate tensile strength of the CFRP plate, 5% and 10% tensile steel rebar corrosion ratio of mass loss and 10% and 20% anchor corrosion ratio in the chloride environment. The evolution of time-dependent prestress losses in the strengthened beam was determined, and the flexural behaviour of the strengthened beams was analysed. A theoretical model is proposed to predict the flexural strength of prestressed CFRP strengthened RC beams in a chloride environment. The experimental results indicated that the coupling of the corrosion expansion of the metal anchor and rebar in the chloride environment had a large negative effect on the flexural performance of the beams strengthened by the self-anchored prestressed CFRP plates. After exposure to the chloride ion solution, the failure mode of the RC beams strengthened by the prestressed CFRP changed from concrete crushing in the compression section to anchor pullout. The proposed model, which considered the effect of a chloride environment to predict the flexural strength of the strengthened beams, agreed well with the test results.</p>

Research on the Fatigue Flexural Performance of RC Beams Attacked by Salt Spray

Influence of Longitudinal Bar Corrosion on Impact Behavior of RC Beams

Flexural Behavior and Durability Properties of Recycled Aggregate Concrete (RAC) Beams Subjected to Long-Term Loading and Chloride Attacks

CFRP Strengthened RC Beams with Pre-Strengthening Non-Uniform Reinforcement Corrosion Subjected to Post-Strengthening Wetting/drying Cycles

Stiffness Degradation for Fatigue of Reinforced Concrete Beams after Electrochemical Rehabilitation

Experimental study on flexural capacity of reinforced concrete beams in marine environment

Performance of Reinforced Concrete Beams Corroded under Sustained Service Loads: A Comparative Study of Two Accelerated Corrosion Techniques

Crack Propagation and Flexural Behaviour of Rc Beams under Simultaneous Sustained Loading and Steel Corrosion

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Study on Degradation Regularity of Bearing Capacity of RC Beams under Corrosive Conditions

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Monotonic and fatigue behavior of steel-concrete composite beams subjected to corrosion

Effect of Chloride-Induced Reinforcing Steel Corrosion on the Flexural Strength of Reinforced Concrete Beams

FLEXURAL CAPACITY OF CORROSION-DAMAGED RC BEAMS

Experimental Research on Fatigue Performance of Reinforced Concrete T-Shaped Beams under Corrosion-Fatigue Coupling Action

Cracking Behavior of Cfrp Laminate-Strengthened Rc Beams with Premechanical and Postmechanical Environmental Damage

Interface Shear Stress of Concrete Beams Strengthened with FRP in Salt Water

Effect of the chloride environmental exposure on the flexural performance of strengthened RC beams with self-anchored prestressed CFRP plates

Effects of exposure in seawater sea-sand concrete pore solution on fatigue performance of carbon FRP bars

EXPERIMENTAL INVESTIGATION AND DESIGN OF SEVERELY CORRODED REINFORCED CONCRETE BEAMS

Coupled Thermo‐hydro‐mechanical Analysis of Reinforced Concrete Beams under the Effect of Frost Damage and Sustained Load