Abstract:To accurately obtain the performance of concrete structures in coastal regions, it is necessary to correctly understand the damage evolution law of reinforced concrete (RC) members under real working conditions. In this paper, four RC beams, subjected to different levels of corrosion and sustained load, are first tested. Reinforcement corrosion coupled with sustained load increases the number and width of cracks at the soffit of beams but decreases their loading capacities. Crack width of the corroded beam under 50% of designed load is two times of that under 30% of designed load. Residual loading capacities of the corroded beams subjected to 30% and 50% of designed load are 87.5% and 81.8% of the control beam. A finite element model is developed for the corroded RC beams. Due to less confinement, concrete below and at the sides of reinforcements is subjected to a higher stress, compared to concrete above the reinforcements. Corrosion expansion of reinforcements is successfully modelled by a temperature-filed method, as it properly simulates the damage evolution of the corroded RC beams. As a result, concrete cracking, caused by the reinforcement corrosion, is well captured. Coupling reinforcement corrosion with sustained load significantly increases the damage level in RC beams, particularly for those subjected to a high sustained load. The whole damage evolution process of concrete cracking due to corrosion expansion under the coupling effect of sustained loading and environment can be simulated, thus providing a reference for the durability evaluation, life prediction, and numerical simulation of concrete structure.

FLEXURAL CAPACITY OF CORROSION-DAMAGED RC BEAMS

Influence of Longitudinal Bar Corrosion on Impact Behavior of RC Beams

Evaluation of Main Code Models for Predicting Flexural Load-Bearing Capacity Against Intermediate Crack-Induced Debonding in Frp-Strengthened Rc Beams

Assesment of Main Models for Predicting Debonding Load-Bearing Capacity Against Intermediate Crack-Induced Debonding Failure in Frp-Strengthened Rc Beams

Deflection and Crack Calculation of Corroded Reinforced Concrete Beams

A New Flexural Strength Model of CFRP-strengthened RC Beams with Intermediate Crack Induced Debonding Failure

Crack Propagation and Flexural Behaviour of Rc Beams under Simultaneous Sustained Loading and Steel Corrosion

Effect of Chloride-Induced Reinforcing Steel Corrosion on the Flexural Strength of Reinforced Concrete Beams

CFRP Strengthened RC Beams with Pre-Strengthening Non-Uniform Reinforcement Corrosion Subjected to Post-Strengthening Wetting/drying Cycles

Flexural Behavior of Corroded Concrete Beams Strengthened with Carbon Fiber-Reinforced Polymer

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Effect of Corrosion on Bond Behavior and Bending Strength of Reinforced Concrete Beams

Influence of pitting corrosion on the bending capacity of reinforced concrete beams

Study on Degradation Regularity of Bearing Capacity of RC Beams under Corrosive Conditions

Residual strengths of reinforced concrete beams with heavy deterioration

Analytical Model to Predict Residual Flexural Capacity of Recycled Aggregate Concrete Beams with Corroded Longitudinal Rebars

Experimental study on flexural capacity of reinforced concrete beams in marine environment

Performance of Reinforced Concrete Beams Corroded under Sustained Service Loads: A Comparative Study of Two Accelerated Corrosion Techniques

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Damage Evolution Of Rc Beams Under Simultaneous Reinforcement Corrosion And Sustained Load

Experimental Investigation on Effective Bond Length of Flexurally Cfrp-Strengthened Rc Beams Failed by Intermediate Crack Debonding