Brazing of SiO2-BN Modified with in Situ Synthesized CNTs to Ti6Al4V Alloy by TiZrNiCu Brazing Alloy

J. Ba,X. H. Zheng,R. Ning,J. H. Lin,J. L. Qi,J. Cao,W. Cai,J. C. Feng

DOI: https://doi.org/10.1016/j.ceramint.2018.03.018

IF: 5.532

2018-01-01

Ceramics International

Abstract:Brazing SiO2-BN ceramic to Ti6Al4V is often associated with the problem of brittle continuous phases and high residual stress at the reaction layer of SiO2-BN, inducing low joining strength. To overcome these problems, SiO2-BN ceramic modified with in situ synthesized carbon nanotubes (CNTs) were joined to Ti6Al4V by TiZrNiCu alloy. Results show that CNTs can improve the wettability of TiZrNiCu on SiO2-BN rapidly, and break the continuous reaction layer of SiO2-BN into fine sizes. Residual stress can also be reduced by low CTE of CNTs and fine size phases among reaction layer. The shear strength of SiO2-BN/Ti6Al4V joints with CNTs modified is 35.3 MPa at 970 degrees C for 10 min, which is 3 times higher than that of the joints without CNTs modified.