Spray Deposition of AgBiS2 and Cu3BiS3 Thin Films for Photovoltaic Applications

Narendra Pai,Jianfeng Lu,Dimuthu C. Senevirathna,Anthony S. R. Chesman,Thomas Gengenbach,Manjunath Chatti,Udo Bach,Philip C. Andrews,Leone Spiccia,Yi-Bing Cheng,Alexandr N. Simonov
DOI: https://doi.org/10.1039/c7tc05711c
IF: 6.4
2018-01-01
Journal of Materials Chemistry C
Abstract:Spray pyrolysis of bismuth(III) tris(4-methylbenzodithioate) toluene solutions containing either silver(I) acetate and 1-octanethiol, or copper(I) acetate and 1,2-ethanedithiol is introduced as a low-temperature solution-based method to produce sub-100 nm thick coatings of alpha cubic rock salt AgBiS2 or orthorhombic Cu3BiS3, respectively. The structure, morphology and optoelectronic properties of the materials thus obtained have been comprehensively characterised using conventional techniques. Extensive optimisation of the deposition conditions has been undertaken to achieve the formation of uniform, 60-70 nm thick films of densely packed AgBiS2 and Cu3BiS3 crystallites with a typical size of 10-20 nm. Planar photovoltaic devices based on spray-deposited AgBiS2 as a light harvester, ZnO as an electron transporting layer, and spiro-OMeTAD as a hole transporting material produce short-circuit current densities as high as 18.1 +/- 0.6 mA cm(-2) under 1 sun AM 1.5 G irradiation. The devices are stable without encapsulation under ambient conditions for at least 1 month.
What problem does this paper attempt to address?