Abstract:During plasma spraying, SiC particles undergo sublimation, accompanied by the sublimation and decomposition of Si and C atoms in the crystal lattice. Ultimately, the deposited SiC either spreads splash or breaks apart on the surface of the carbon‐carbon composite matrix. It is widely known that silicon carbide (SiC) is challenging to thermal spray. However, the nature of deposition and the underlying mechanisms are still not clearly understood. In the current work, the process of atmospheric plasma‐sprayed SiC was investigated in detail. SiC exhibits sublimation severely under the plasma spraying (PS). More than 65 mol.% SiC particles lost by sublimation during PS estimated by calculation. Due to the nonuniformity of temperature in plasma flame, a small amount of SiC particles was retained. Moreover, a small amount of Si and SiO2 was experimentally observed after deposition process from the single‐splat characterization. According to the first‐principles calculations, the detachment energy of C atom from the lattice (0.591 eV) is lower than that of Si atom (1.257 eV). The adsorption energies of an O atom on the Si‐ and C‐terminated surfaces are −9.549 and −7.631 eV, respectively. Therefore, C is more likely to form gaseous products after decomposition, and Si is more likely to be retained to form Si and SiO2. Mullite was found on the grain boundaries of molten Si, which was attributed to the rapid diffusion of the Al2O3 substrate along the grain boundaries of Si, promoting the spreading of molten splats. It is difficult to stack particles through self‐diffusion among SiC particles to form coatings. The discovery on thermal deposition mechanism of SiC in PS is helpful to promote the practical application of SiC coatings on preparation optimization and interfacial bonding improvement.

Spraying power influence on microstructure and bonding strength of ZrSi 2 coating for SiC coated carbon/carbon composites

Spraying Power Effect on Micro-Structure and Mechanical Property of TaSi2 Coating Prepared by Supersonic Air Plasma Spraying for SiC-Coated C/C Composites

Effects of SiC on microstructure and properties of plasma sprayed ZrB2–ZrC composite coating

Preparation and properties of supersonic atmospheric plasma sprayed TiB2−SiC coating

Microstructural study of nanostructured Zro 2 based thermal barrier coatings fabricated by high efficiency supersonic plasma spraying

Synthesis of In Situ ZrB2-SiC-ZrC Coating on ZrC-SiC Substrate by Reactive Plasma Spraying

Oxidation ablation resistance of ZrB2-HfB2-SiC-TaSi2 coating prepared on C/C composite surface

Effect of spraying power on microstructure and properties of supersonic plasma sprayed Al2O3 coating on porous Si 3N4 substrate

Microstructure characterization of in-situ ZrC composite coating with graceful toughness and improved tribological properties prepared by plasma spraying

Ablation Mechanism and Elevated Ablation Resistance of In-Situ Zrc-Zrsi2 Composite Coating Prepared by Plasma Spraying

TEM Exploration of In-Situ Nanostructured Composite Coating Fabricated by Plasma Spraying 8Ysz-Al-sic Composite Powder

Microstructure and Ablation Behavior of W/ZrC/SiC Coating on C/C Composites Prepared by Reactive Melt Infiltration and Atmospheric Plasma Spraying

Static Ablation Resistance of ZrB2-SiC Composite Coatings Prepared by Atmospheric Plasma Spraying

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Effect of Si, Al2O3 additives on the ablation behavior of ZrB2-SiC coating with Al2O3-modified SiC bond coat for C/C composites

Low-pressure plasma spraying of ZrB2-SiC coatings on C/C substrate by adding TaSi2

Deposition behavior and mechanism of thermal sprayed SiC

Microstructure and properties of Cr7C3-CrSi2 composite coatings prepared by plasma spraying

Anti-ablation Performance of Plasma Sprayed ZrB2/SiC Coatings on C/C Substrates and the Influence of a Chemical Vapor Deposited SiC Interlayer

Effect of Submicron and Nano SiC Particles on Erosion Wear and Scratch Behavior of Plasma-Sprayed Al 2 O 3 /8YSZ Coatings

Characteristics of ZrC Barrier Coating on SiC-Coated Carbon/Carbon Composite Developed by Thermal Spray Process