Abstract:A thermally sprayed deposit is formed by a stream of molten droplets impacting on a substrate followed by flattening, rapid solidification, and cooling processes. The individual molten droplets spread into thin lamellae, the stacking of which rudimentarily constitutes the thermal spray deposit. Accordingly, a thermally sprayed deposit is generally composed of lamellar structure. A portion of the deposit are voids, which constitute up to 20% of the total volume [1]. Some of the voids originated from insufficient liquid filling, prior to complete solidification, and incomplete wetting of molten liquid on the prior deposited lamella surfaces. Microcracks can be formed easily in the splats of brittle materials, in particular, ceramics owing to the quenching stresses that occur in splats [2]. Such microcracks are also a type of void within the deposits, and constitute a fraction of the overall porosity. The existence of voids in the coating will degrade the mechanical performance and corrosion resistance of thermal sprayed materials to a relatively low level compared to corresponding bulk materials. When a thermal sprayed coating is used under a certain mechanical loading, the loading may cause coating delamination or spallation in service owing to low adhesion of the coating to the substrate and limited cohesion within the coating. This undoubtedly leads to a decrease in the coating’s effective thickness or even direct exposure of the substrate surface to the operating environment. Many studies have revealed that the failure of the coating occurs readily from the interfaces among lamellae in the coating, and the interfaces between the coating and the substrate, for example, under localized load such as in abrasive wear [3] or erosion [4], fretting wear [5] and fracture mechanics test [6]. Even during the preparation of thermal sprayed samples for microstructure examination, pullouts do occur [7]. Such effect is attributed to the pores in the coating existing in the form of non-bonded lamellar interfaces [8], although in thermal barrier coatings (TBC), the performance may be improved by the existence of pores in the coating. Therefore, the modification of the microstructure of as-sprayed coating is desirable to improve coating performance. Up to now, many attempts

Effect of spraying power on microstructure and properties of supersonic plasma sprayed Al2O3 coating on porous Si 3N4 substrate

Fabrication and properties of supersonic plasma sprayed Al2O3 coating on porous Si3N4 substrate

Effect of Spraying Power on the Microstructure and Mechanical Properties of Supersonic Plasma-Sprayed Ni-based Alloy Coatings

Effect of Spraying Power on Microstructure and Bonding Strength of Mosi2-Based Coatings Prepared by Supersonic Plasma Spraying

Effect of Spraying Power on Oxidation Resistance and Mechanical Properties of Plasma Sprayed La-Mo-Si Coating

Spraying Power Effect on Micro-Structure and Mechanical Property of TaSi2 Coating Prepared by Supersonic Air Plasma Spraying for SiC-Coated C/C Composites

Effect of Suspension Plasma Spraying Power on the Microstructure and Properties of Cr2AlC Coatings

Plasma sprayed CoNiCrMoNb(BSi) high-entropy amorphous alloy coating: The effect of spraying power on microstructure, mechanical and tribological properties

Effects of Spray Parameters on the Microstructure and Property of Al2O3 Coatings Sprayed by a Low Power Plasma Torch with a Novel Hollow Cathode

Effect of Spraying Parameters on the Microstructure and Mechanical Properties of Micro-Plasma Sprayed Alumina-Titania Coatings

Microstructural and Porosity Variations in the Plasma-Sprayed Ni-Alloy Coatings Prepared at Different Spraying Powers

Microstructure and properties of multi-function micro-plasma sprayed Al2O3 coatings

Effect of suspension plasma spraying power on the microstructure and properties of Cr 2 AlC coatings

Microstructure, formation mechanism and properties of plasma-sprayed Cr7C3—CrSi2—Al2O3 coatings

Spraying power influence on microstructure and bonding strength of ZrSi 2 coating for SiC coated carbon/carbon composites

Microstructures and Wear Resistance of Al-25 wt.%Si Coatings Prepared by High-Efficiency Supersonic Plasma Spraying

Effect of the Powder Particle Structure and Substrate Hardness During Vacuum Cold Spraying of Al2O3

Effect of Critical Plasma Spray Parameter on Complex Permittivity and Microstructure by Plasma Spraying Cr/Al2o3 Coatings

Potential strengthening of erosion performance of plasma-sprayed Al2O3 coating by adhesives impregnation

Structure and Properties of MoSi2-CoNiCrAlY Nano-composite Coating by Plasma Spraying