Abstract:This study demonstrates the use of continuous supercritical hydrothermal synthesis (CSHS) for producing active and stable nickel nanocatalysts employed in supercritical water gasification (SCWG), which generates hydrogen-rich syngas from biomass. The investigation focused on synthesizing a catalyst material comprising active nickel and a magnesium/aluminum-mixed additive using CSHS. The impact of synthesis temperature on the properties of the product was initially assessed by synthesizing a series of Ni-Mg-Al mixed particles at temperatures ranging from 350 to 500 °C under a constant pressure of 25 MPa. Needle-like nanocrystal bundles mainly composed of AlOOH were successfully obtained, exhibiting high specific surface areas (88–119 m2/g) and demonstrating highly dispersed Ni, Mg, and Al elements as confirmed by TEM-EDS analysis. Increasing the temperature of CSHS resulted in higher product crystallinity and an increased conversion rate of Ni2+ precursor, from 87.4 % at 350 °C to 95.9 % at 500 °C. Another series of Ni/Mg-Al-O catalysts with varying Mg/Al contents was synthesized at 500 °C and 25 MPa, and evaluated for SCWG of 5 wt% glucose at 500 °C. Due to the well-dispersed components, these catalysts exhibited remarkable and identical activities, resulting in a significant increase in H2 yield from 0.9 mol/mol without a catalyst to 3.4–3.9 mol/mol, as well as an enhancement in carbon gasification efficiency from 24.6 % to 71.3–72.9 %, when loaded with a catalyst loading of 10 wt% glucose. An optimized composition of Mg/Al was determined, comprising 30 % Mg2+ and 40 % Al3+ species, due to the formation of an appropriate quantity of Mg-Al crystalline species through the CSHS approach. This catalyst exhibited the highest specific surface area and demonstrated remarkable stability in terms of crystalline and pore structures during the SCWG use. We conclude that CSHS is an effective approach for synthesizing active and stable metal nanocatalysts with excellent property stability for SCWG applications.

Stability and Activity Maintenance of Al2O3- and Carbon Nanotube-Supported Ni Catalysts During Continuous Gasification of Glycerol in Supercritical Water

Stability and Activity Maintenance of Sol-Gel Ni-MxOy (M = Ti, Zr, Ta) Catalysts During Continuous Gasification of Glycerol in Supercritical Water

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Stability and Activity of a Co-Precipitated Mg Promoted Ni/Al2O3 Catalyst for Supercritical Water Gasification of Biomass

Catalytic Performances of Ni-based Catalysts on Supercritical Water Gasification of Phenol Solution and Coal-Gasification Wastewater

Behavior of Nickel Catalysts in Supercritical Water Gasification of Glucose: Influence of Support

Nickel nanocatalysts prepared via continuous supercritical hydrothermal synthesis for supercritical water gasification

Efficient and Stable Supercritical-Water-synthesized Ni-based Catalysts for Supercritical Water Gasification

Co-precipitated Ni–Mg–Al Catalysts for Hydrogen Production by Supercritical Water Gasification of Glucose

Deciphering the Stability Mechanism of Pt-Ni/Al2O3 Catalysts in Syngas Production Via DRM

Partial Oxidation Of Methane To Syngas Over Ni-Based Catalysts

Ni-based catalysts supported on MgAl<sub>2</sub>O<sub>4</sub> with different properties for combined steam and CO<sub>2</sub> reforming of methane

Activity and stability of nickel based MCM-41 methanation catalysts for production of synthetic natural gas

Nanocatalysts Anchored on Nanofiber Support for High Syngas Production Via Methane Partial Oxidation

Hydrogen Production by Biomass Gasification in Supercritical Water over Ni/γAl2O3 and Ni/CeO2-γAl2O3 Catalysts

Inspection over Carbon Deposition Features of Various Nickel Catalysts During Simulated Biogas Dry Reforming

Study on Methanation Performance of Biomass Gasification Syngas Based on a Ni/Al2O3 Monolithic Catalyst

Hydrogen production by biomass gasification in supercritical water over Ni/ gamma Al sub (2 O) sub (3) and Ni/CeO sub (2 gamma Al) sub (2) O sub (3 catalysts)

Partial oxidation of ethane to syngas over nickel‐based catalysts modified by alkali metal oxide and rare earth metal oxide

Effect of Nanostructured Supports on Catalytic Methane Decomposition

Influence of Nitrogen on the Catalytic Behaviour of Pt/γ-Al2O3 Catalyst in Glycerol Reforming Process