Abstract:This study demonstrates the use of continuous supercritical hydrothermal synthesis (CSHS) for producing active and stable nickel nanocatalysts employed in supercritical water gasification (SCWG), which generates hydrogen-rich syngas from biomass. The investigation focused on synthesizing a catalyst material comprising active nickel and a magnesium/aluminum-mixed additive using CSHS. The impact of synthesis temperature on the properties of the product was initially assessed by synthesizing a series of Ni-Mg-Al mixed particles at temperatures ranging from 350 to 500 °C under a constant pressure of 25 MPa. Needle-like nanocrystal bundles mainly composed of AlOOH were successfully obtained, exhibiting high specific surface areas (88–119 m2/g) and demonstrating highly dispersed Ni, Mg, and Al elements as confirmed by TEM-EDS analysis. Increasing the temperature of CSHS resulted in higher product crystallinity and an increased conversion rate of Ni2+ precursor, from 87.4 % at 350 °C to 95.9 % at 500 °C. Another series of Ni/Mg-Al-O catalysts with varying Mg/Al contents was synthesized at 500 °C and 25 MPa, and evaluated for SCWG of 5 wt% glucose at 500 °C. Due to the well-dispersed components, these catalysts exhibited remarkable and identical activities, resulting in a significant increase in H2 yield from 0.9 mol/mol without a catalyst to 3.4–3.9 mol/mol, as well as an enhancement in carbon gasification efficiency from 24.6 % to 71.3–72.9 %, when loaded with a catalyst loading of 10 wt% glucose. An optimized composition of Mg/Al was determined, comprising 30 % Mg2+ and 40 % Al3+ species, due to the formation of an appropriate quantity of Mg-Al crystalline species through the CSHS approach. This catalyst exhibited the highest specific surface area and demonstrated remarkable stability in terms of crystalline and pore structures during the SCWG use. We conclude that CSHS is an effective approach for synthesizing active and stable metal nanocatalysts with excellent property stability for SCWG applications.

Stability and Activity of a Co-Precipitated Mg Promoted Ni/Al2O3 Catalyst for Supercritical Water Gasification of Biomass

Efficient and Stable Supercritical-Water-synthesized Ni-based Catalysts for Supercritical Water Gasification

Nickel nanocatalysts prepared via continuous supercritical hydrothermal synthesis for supercritical water gasification

Catalysis in Supercritical Water Gasification of Biomass: Status and Prospects

Investigation of Catalysts, CO 2 Sorbents and Their Combinations for Maximising H 2 Output During the Thermal Decomposition of Biomass

Hydrothermal Gasification of Phenol Water on Novel Carbon-Supported Ni Catalysts Prepared by the Sol-Gel Method Using PEG

Studies of CO2 gasification of the Miscanthus giganteus biomass over Ni/Al2O3-SiO2 and Ni/Al2O3-SiO2 with K2O promoter as catalysts

Molecular Dynamics Simulations Guide the Gasification Process of Carbon-Supported Nickel Catalysts in Biomass Supercritical Water

Catalytic Hydropyrolysis of Lignin Using NiMo-doped Catalysts: Catalyst Evaluation and Mechanism Analysis

Catalytic gasification of food waste in supercritical water over La promoted Ni/Al2O3 catalysts for enhancing H2 production

Study on Methanation Performance of Biomass Gasification Syngas Based on a Ni/Al2O3 Monolithic Catalyst

Catalytic gasification of phenol in supercritical water over bimetallic Co–Ni/AC catalyst

Light Promotion and Different Reaction Pathways Enhance Photothermocatalytic Syngas Production for Cellulose Steam Reforming Over Ni/θ‐Al2O3

Boosting syngas production from corncob tar reforming over Ni/MgAl hydrotalcite-derived catalysts

High stable NiCoAl catalyst prepared by combustion method for the hydrodeoxygenation of lignin-derived phenolic compounds: Effect of calcination temperature

Inspection over Carbon Deposition Features of Various Nickel Catalysts During Simulated Biogas Dry Reforming

Catalysis/sorption enhanced pyrolysis-gasification of biomass for H 2 -rich gas production: Effects of various nickel-based catalysts addition and the combination with calcined dolomite

ReaxFF molecular dynamics simulation of nickel catalysed gasification of cellulose in supercritical water

The influence of supported Ni catalysts on the product gas distribution and H2 yield during cellulose pyrolysis

Catalytic Properties and Recycling of NiFe2O4 Catalyst for Hydrogen Production by Supercritical Water Gasification of Eucalyptus Wood Chips

CO Rich Syngas Production from Catalytic CO2 Gasification-Reforming of Biomass Components on Ni/CeO2