Abstract:In this work, we studied the microstructure and mechanical properties of hot-pressed B4C, B4C + 5 wt% TiAl, and B4C + B + 5 wt% TiAl. The X-ray diffraction and Raman spectroscopy results showed that the addition of Ti–Al alone did not led to Al doping in B4C, and it did not reduce the degree of amorphization of B4C generated under high shear stresses. In contrast, the co-addition of Ti–Al and B resulted in both B and Al solid solutions in the B4C and effectively mitigated the amorphization of B4C. Electron probe microanalysis (EPMA) and energy dispersive X-ray spectroscopy (EDS) analyses suggested that the co-addition of Ti–Al and B promoted the interdiffusion of lightweight elements such as B, C, Al, Mg, and Si at high temperatures, resulting in a dense body with uniformly distributed second phase. The transmission electron microscopy (TEM) observations of the B4C + B + 5 wt% TiAl sample showed that a nano–core–shell structure with aggregated dislocations in the shells which was generated at TiB2 grains due to the segregation and dissolution-precipitation between TiB2 and B-rich boron carbide. The short-range ordered substitution of B and the disordered doping of Al in B4C led to lattice distortion and expansion, resulting in the formation of high-density defects, including stacking faults and nano-twins, improving the mechanical properties for B4C. The B4C + B + 5 wt% TiAl sample exhibits a combination of fascinating properties, including low density (2.52 g/cm3), high Vickers hardness (35.53 ± 0.83 GPa) and moderate fracture toughness (4.37 ± 0.35 MPa m1/2).

Effects of Al Addition on the Phase Transformation and Interfacial Evolution in Multilayer Ti-B4C Composite

Improvement on Mechanical Property of B4C/Al Composites by Addition of Ti Through Interfacial Reaction

The effect of B and Ti–Al intermetallics additions on the microstructure and mechanical properties of hot-pressed B4C

Effect of Al content on impact resistance behavior of Al-Ti-B4C composite fabricated under air atmosphere

Preparation and toughness mechanism of in-situ Ti3AlC2 enhanced and toughened TiAl3 matrix composites

Study on the enhancement mechanism of (TiC + B 4 C)/6061Al composite fabricated via vacuum hot-press sintering

Effect of Ti Content and Stirring Time on Microstructure and Mechanical Behavior of Al-B4C Composites

Fabrication, microstructure and mechanical properties of TiAl matrix composite reinforced by submicro/nano-Ti 2 AlC

Mechanical Properties and Microstructure of Al2o3/Tial in Situ Composites Doped with Cr2o3

Effect of Heat Treatment on the Microstructure and Properties of Ti3AlC2-Cr2AlC-TiC Composite

Effectively enhanced strength by interfacial reactions in in-situ carbon reinforced Al matrix composites

Microstructure and Mechanical Properties of Ti2AlC-reinforced TiAl Composites

Fabrication of Al/Al-TiB 2 laminate composites via hot press sintering process: An insight into the mechanical properties and fracture behavior

Anisotropic microstructures and mechanical properties of textured Ti3AlC2/TiAl3/Al composite

Strength improvement and fracture mechanism in Fe40Al/TiC composites with high content of TiC

Mechanical Properties and Microstructure of Al2O3/TiAl in Situ Composites Doped with Cr

Effect of Nb addition on the microstructure and mechanical properties of additively manufactured Ti2AlC MAX-phase ceramic matrix composites

Simultaneous Improvement in Strength and Ductility of TC4 Matrix Composites Reinforced with Ti1400 Alloy and In Situ-Synthesized TiC

Reaction mechanism and microstructure evolution of superhigh strength in-situ TiC/Ti composite based on Cr 2 AlC-Ti system

Revealing the formation, strengthening and toughening mechanism of a new (Ti3AlC2+Al2O3)p /Al3Ti composite with strength-ductility synergy

In-Situ Observation of Fracture Behavior of Ti-Aluminide Multi-Layered Composites Produced by a Hybrid Sintering Process