A Simple Efficient Polysulfide Anchor for Li-S Batteries
Zhangxiang Hao,Lixia Yuan,Yunhui Huang
DOI: https://doi.org/10.1149/ma2016-02/5/841
2016-01-01
ECS Meeting Abstracts
Abstract:The popularization of electric vehicles requires the development of low-cost rechargeable batteries with safety and high energy density. Lithium-sulfur (Li-S) battery stands as an important candidate for next-generation high-energy secondary batteries due to its high specific capacity, low cost and environmental friendliness. But the realization of lithium sulfur battery suffers from the poor rechargeability, low rate capability and short life span of sulfur cathode. In order to overcome the hurdles, various approaches have been proposed that can be classified into three categories: (1) confining the intermediates Li2Sx (3≤x≤8) within the cathode through material or electrode design, (2) modifying the liquid electrolyte or employing solid electrolytes, and (3) protecting the anode via coatings and electrolyte additives. Among them, some kinds of metal oxides, metal sulfides, or some two-dimensional layered materials which have strong anchoring effect for polysulfides, can immobilize sulfur species more efficiently than the widely-used carbon materials. But, most fabrication of the nano-architectured absorbents usually requires complicated procedures, which may greatly limit the manufacturability of S cathode. Herein, we report a novel polysulfides adsorption matrix for high performance Li-S batteries via a super facile process of synthesis. An ordinary commercial titanium nitride (TiN), after a simple corrosion process, can work as a high-efficiency matrix to immobilize sulfur thus a largely improved cycle stability can be achieved. Here the TiN matrix has three enormous advantages: ⅰ) a super high conductivity as 1000 S cm-1 at 298 K, ⅱ) containing polar Ti-N units which have strong binding for lithium polysulfides, and ⅲ) low cost and environmentally friendly. The S/TiN cathode, with 70 wt.% sulfur content, reveals a high initial reversible capacity of 1087 mAh g-1 at 0.5 C and a long-term charge/discharge process of 400 cycles at 0.5 C, with a decay rate of 0.19 % per cycle. Furthermore, the reversible discharge capacity is above 600 mAh g-1 even at 5 C rate. References [1] P.G. Bruce, S.A. Freunberger, L.J. Hardwick, J.M. Tarascon, Nat. Mater. 11 (2012) 19-29. [2] A. Manthiram, S.H. Chung, C. Zu, Adv. Mater. 27 (2015) 1980-2006. [3] Y. Zhao, Y. Ding, Y. Li, L. Peng, H.R. Byon, J.B. Goodenough, G. Yu, Chem. Soc. Rev. 44 (2015) 7968-7996. Figure 1