Abstract:Tin-based alloy solder joints are an indispensable key part of electronic products and the basis of realizing the functionalization of electronic components. The failure of an electronic product is often caused by solder joint damage. Life prediction of the solder joint is of great significance for the reliability research of electronic products. The intermetallic compound (IMC) thickness is an important parameter to evaluate the quality of solder joints. This study takes the thickness of the IMC layer and the assembly solder joints of the 62Sn36Pb2Ag QFP device as the key performance degradation parameter and the research object, respectively. After the reflowing process, Cu6Sn5 and Cu3Sn IMC phases were observed at the copper lead side, and the (CuxNi1-x)6Sn5 phase was observed at the PCB side. The evolution of interfacial microstructures was observed by a scanning electron microscope (SEM). The thickness of the IMC layer after storage at 94, 120, and 150 °C for different periods (1, 4, 9, 16, 25, 36, 49 days) was monitored. The growth process of the IMC is controlled by diffusion. As the storage time increases, the thickness of the IMC layer gradually increases. The growth rate of the IMC layer increases with the increase of the storage temperature because of the higher diffusion coefficient. Based on the Arrhenius equation, the growth kinetics model of the IMC with a bilateral interface is established. The failure density function is obtained by fitting the initial IMC thickness with a normal distribution, and the reliability function is then obtained to predict the long-term storage failure life of QFP assembly solder joints. Finally, this work calculates the median life and characteristic life of QFP assembly solder joints to be 16092 years and 17471 years, respectively. These results are expected to provide a new way to predict the life of solder joints stored for a long time and provide experimental and data support for the reliable application of the 62Sn36Pb2Ag solder.

Reliability Prediction Of Different Size Solder Bumps In Thermal Shock Test Using Fem

Dynamic Substructure Method for Prediction of Solder Joint Reliability of IC Package under Drop Test

Predicting fatigue life of Solder joint with submodel method for a BGA package

Finite Element Analyses and Lifetime Predictions for Snagcu Solder Interconnections in Thermal Shock Tests

Finite Element Simulation Of The Size Effect On Thermal Fatigue Behavior Of Solder Bump Joints In Tsv Structure

Interposer Connection Reliability Using Double-Side Solder Bump for Board-Level Vertical Interconnection

Shape Prediction of BGA Solder Joint and Its Reliability Optimization Design

Research on the reliability of Micro LED high-density solder joints under thermal cycling conditions

Failure Mechanism and Predictive Modeling for Microbump Interconnects Drop Life Under Diverse Impact Angles in Advanced Packaging

Thermal Cycling Life Prediction of Sn-3.0Ag-0.5Cu Solder Joint Using Type-I Censored Data

An Improved Substructure Method For Prediction Of Solder Joint Reliability In Thermal Cycle

Mechanical and Electrical Reliability Assessment of Bump-Less Wafer-on-wafer Integration with One-Time Bottom-Up TSV Filling

Finite element method and experimental study on life prediction of lead-free BGA solder joints using an energy-based approach

Long-term Storage Life Prediction and Growth Kinetics of Intermetallic Compounds in 62sn36pb2ag Solder Joints

Thermal Fatigue Analysis of Microbumps in a 3D TSV Integration Device

Reliability Study of Fine Pitch Cu-Sn Micro-Bump Structure Electromigration Test by Finite Element Simulation

Experimental and numerical analysis of BGA lead-free solder joint reliability under board-level drop impact

Research on the Reliability of Cu/Sn Copper Pillar Bump

Prediction of Solder Bump Formation in Solder Jet Packaging Process

Shape Prediction and Reliability Design of Ball Grid Array Solder Joints

Influence of Solder Cap Thickness on the Interfacial Reaction in Cu/Sn/Ni Copper Pillar Bump