The Synthesis of Large-Diameter Znte Crystal for Thz Emitting and Detection

Hang Liu,Wei Bai,Jiatai Feng,Wanqi Jie

DOI: https://doi.org/10.1016/j.jcrysgro.2017.06.009

IF: 1.8

2017-01-01

Journal of Crystal Growth

Abstract:A high-quality, large-size ZnTe ingot with the diameter of 60mm and the length of 80mm were prepared by the modified temperature gradient solvent method, where the Te rich solution acted as both solubility promoter and reactant. Using this method, the crystallization temperature was reduced from 1568K to 1333K, plus, the crystal defects could be reduced in some extent due to the lower zinc partial pressure. Few Te inclusions are found in the as-grown ZnTe crystal with the bulk factor less than 0.1%. X-ray diffraction (XRD), infrared transmission microscope, fourier transform infrared (FT-IR) spectrometer, ultraviolet–visible (UV–Vis) spectrophotometer were used to analyze the qualities and properties of the ZnTe crystals. The infrared transmittance over the wavenumber range from 500 to 4000cm−1 is about 60% and the band gap is about 2.23eV at the room temperature. The FWHM of the detection pulse with the THz time-domain spectroscopy (THz-TDS) is about 0.34ps. Besides, both the radiation and detection pulse have a wide frequency distribution about 3THz at the room temperature. These results strongly indicate that the high-quality ZnTe crystal synthesized by the temperature gradient solvent method is superior for THz device applications.