Abstract:Porous silicon nitride ceramics with a biomorphic microstructure were manufactured by car- bothermal reduction and nitridation of Y_2O_3/SiO_2/charcoal composites in high concentration nitrogen atmospheres(0.6MPa) at 1600℃.These composites were prepared from pine-derived charcoal impreg- nated with yttrium-incorporated silica mixed sol by vacuum/pressure infiltration process.The influences of sintering temperature,reaction time,additive and sintering atmosphere on microstructure and phase composition were studied by XRD,SEM.The formation mechanism of Si_3N_4 was analyzed.XRD analy- sis shows that mainlyβ-Si_3N_4 and minor glass component of YsSi_4N_4O_(14) are detected.SEM observation reveals that the resulting porous Si_3N_4 retains the microcellular morphology of original pinewood tissue, and the remarkable rod-likeβ-Si_3N_4 grains grow from the internal walls of macroscopic pores.The sin- tering process of porousβ-Si_3N_4 consists of three stages,namely,formation of a-Si3N4,transformation ofα-βand grain growth,respectively.Nitridation is based on gas-solid and gas-gas reaction among SiO(g),N_2(g),C(s) or CO(g) for the samples treated at 1450℃.Porous ceramics with elongated fibrousβ-Si_3N_4 grain is developed by solution-reprecipitation mechanism at 1600℃.

Properties of Large-Sized Porous Si3n4 Ceramic Tubes Fabricated by Carbothermal Reduction of Diatomite Preforms

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Microstructure and mechanical properties of porous Si 3 N 4 –SiO 2 ceramics fabricated by a process combining carbothermal reduction and sol–gel infiltration–sintering

Fabrication of Porous Silicon Nitride with High Porosity by Diatomite

Synthesis of Porous Silicon Nitride Ceramics from Diatomite

Fabrication and Properties of Porous Si3N4 Ceramic with High Porosity

Porous TiN Ceramics Fabricated by Carbothermal Reduction Method

Fabrication of High-Porosity Silicon Nitride Ceramics with Excellent Mechanical Properties

Fabrication and Strengthening of Porous Si3N4 Ceramics by Replacement of Oxide Phase with Si3N4 at Grain Boundary Through Carbothermal Nitridation

Fabrication And Properties Of Porous Si3n4-Sio2 Ceramics With Dense Surface And Gradient Pore Distribution

Fabrication and Mechanical Properties of Porous Silicon Nitride Ceramics from Low-Purity Powder

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Porous Silicon Nitride Ceramics Prepared by Reduction – Nitridation of Diatomite

Porous 2h‐silicon Carbide Ceramics Fabricated by Carbothermal Reaction Between Silicon Nitride and Carbon

Effects of Sintering Additives on Properties of Porous Silicon Nitride Ceramics Fabricated by Carbothermal Reduction

A non-sintering fabrication method for porous Si3N4 ceramics via sol hydrothermal process

Porous Silicon Nitride Ceramics Fabricated by Carbothermal Reduction-Reaction Bonding

Biomimetic Synthesis of Porous Si_3N_4 Ceramics

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface

Preparation And Properties Of High Strength Porous Si3n4 Ceramics

Microstructure and Mechanical Properties of Porous SiC Ceramics by Carbothermal Reduction and Subsequent Recrystallization Sintering