Abstract:Porous Si2N2O/SiC ceramics is facilitated at 1200 °C for 10 min by microwave sintering. Rapid in‐situ production of Si2N2O fibers provided high mechanical properties of the samples. The porosity of the prepared sample is tailorable and the thermal insulation effect is excellent. Two steps strategy were taken to effectively produce porous Si2N2O/SiC ceramics: 1) direct foaming combined with sol‐gel curing at room temperature to form a green body, and 2) sintering assisted by in‐situ production of Si2N2O fibers under microwave sintering conditions. Non‐toxic silica sol was used to provide silicon source for in‐situ synthesis of Si2N2O, the silica sol could form a gel that stabilizes the bubbles, creating a porous structure. A thorough investigation was conducted into how different sintering temperatures affected the microstructure, flexural strength, and porosity of the porous Si2N2O/SiC composites. The main bonding phase in the porous composites was the Si2N2O with fiber morphology. The optimal microwave sintering temperature for fabricating porous Si2N2O/SiC ceramics, using a combination of sol‐gel and direct foaming techniques, has been determined to be 1200 °C. At this temperature, the porosity can be controlled between 73.32% and 83.16% by proportionally adjusting the ratio of the raw materials. Under the condition of high porosity, the thermal radiation is dominant and the thermal conductivity increases with the increase of temperature. With the decrease of porosity, the heat conduction is dominant, and the thermal conductivity decreases with the increase of temperature.

Microstructure and mechanical properties of porous Si 3 N 4 –SiO 2 ceramics fabricated by a process combining carbothermal reduction and sol–gel infiltration–sintering

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Fabrication And Properties Of Porous Si3n4-Sio2 Ceramics With Dense Surface And Gradient Pore Distribution

Fabrication of High-Porosity Silicon Nitride Ceramics with Excellent Mechanical Properties

A non-sintering fabrication method for porous Si3N4 ceramics via sol hydrothermal process

Fabrication of Porous Silicon Nitride with High Porosity by Diatomite

Fabrication and Properties of Porous Si3N4 Ceramic with High Porosity

Synthesis of Porous Silicon Nitride Ceramics from Diatomite

Microstructure and Mechanical Properties of Porous SiC Ceramics by Carbothermal Reduction and Subsequent Recrystallization Sintering

Microstructure and Mechanical Properties of Three Porous Si3n4 Ceramics Fabricated by Different Techniques

Properties of Large-Sized Porous Si3n4 Ceramic Tubes Fabricated by Carbothermal Reduction of Diatomite Preforms

Fabrication and Strengthening of Porous Si3N4 Ceramics by Replacement of Oxide Phase with Si3N4 at Grain Boundary Through Carbothermal Nitridation

Fabrication and Mechanical Properties of Porous Silicon Nitride Ceramics from Low-Purity Powder

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface

Fabrication of Porous Silicon Nitride Ceramics with Gradient Microstructure

A new approach for the net-shape fabrication of porous Si3N4 bonded SiC ceramics with high strength

Preparation of Porous Si2N2O/SiC Ceramics by Microwave Sintering

Mechanical and Dielectric Properties of Porous Si3n4-Sio2 Composite Ceramics

Preparation of Porous Si3N4 Ceramics with Controlled Porosity and Microstructure by Fibrous Α‐si3n4 Addition

Porous Silicon Nitride Ceramics Prepared by Reduction – Nitridation of Diatomite

Synthesis and properties of porous SiN/SiC nanocomposites by carbothermal reaction between SiN and carbon