Abstract:With types of in-house-synthesized multi-walled carbon nanotubes (CNTs) and the nitrates of the corresponding metallic components, highly active CNT-promoted Cu–ZnO–Al2O3 catalysts, symbolized as CuiZnjAlk-x%CNTs, were prepared by the co-precipitation method. Their catalytic performance for methanol synthesis from H2/CO/CO2 was studied and compared with the corresponding CNT-free co-precipitated catalyst, CuiZnjAlk. It was shown experimentally that appropriate incorporation of a minor amount of the CNTs into the CuiZnjAlk could significantly increase the catalyst activity for methanol synthesis. Under the reaction conditions of 493 K, 5.0 MPa, H2/CO/CO2/N2 = 62/30/5/3 (v/v), GHSV = 8000 h-1, the observed CO conversion and methanol formation rate over a co-precipitated catalyst of Cu6Zn3Al1-12.5%CNTs reached 36.8% and 0.291 μmol CH3OH s-1 (m2-surf. Cu)-1, which was about 44 and 25% higher than those (25.5% and 0.233 μmol CH3OH s-1 (m2-surf. Cu)-1) over the corresponding CNT-free co-precipitated catalyst, Cu6Zn3Al1. Addition of a minor amount (10–15 wt%) of the CNTs to the Cu6Zn3Al1 catalyst was found to considerably increase specific surface area, especially Cu surface area of the catalyst. H2-TPD measurements revealed that the CNTs and the pre-reduced CNT-promoted catalyst systems could reversibly adsorb and store a considerably greater amount of hydrogen under atmospheric pressure at temperatures ranging from room temperature to ∼573 K. This unique feature would be beneficial for generating microenvironments with higher stationary-state concentration of active hydrogen adspecies on the surface of the functioning catalyst, especially at the interphasial active sites since the highly conductive CNTs might promote hydrogen spillover from the Cu sites to the Cu/Zn interphasial active sites, and thus be favorable for increasing the rate of the CO hydrogenation reactions. Alternatively, the operation temperature for methanol synthesis over the CNT-promoted catalysts can be 15–20 degrees lower than that over the corresponding CNT-free contrast system. This would contribute considerably to an increase in equilibrium CO conversion and CH3OH yield. The results of the present work indicated that the CNTs could serve as an excellent promoter.

Atomic Layer Deposition of Ni on Cu Nanoparticles for Methanol Synthesis from CO2 Hydrogenation

Effect of Ni Content of Ni/-Al2O3 Catalysts Prepared by the Atomic Layer Deposition Method on CO2 Reforming of Methane

Hierarchical hollow Ni/γ-Al2O3 catalyst derived from flower-like Ni-Al layered double hydroxide with stable catalytic performance for CO2 methanation

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

Bimetallic Ni-Co nanoparticles on SiO2 as robust catalyst for CO methanation: Effect of homogeneity of Ni-Co alloy

Development of Highly Stable Ni-Al 2 O 3 Catalysts for CO Methanation

Aqueous Miscible Organic LDH Derived Ni-Based Catalysts for Efficient CO2 Methanation

Improvement of Cu/Zn-based catalysts by nickel additive in methanol decomposition

Preparation of Highly Dispersed Supported Ni-Based Catalysts and Their Catalytic Performance in Low Temperature for CO Methanation

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

Cu/ZnAl2O4 Catalysts Prepared by Ammonia Evaporation Method: Improving Methanol Selectivity in CO2 Hydrogenation Via Regulation of Metal-Support Interaction

Tuning Interfaces between Cu and Oxide via Atomic Layer Deposition Method for CO2 Hydrogenation to Methanol

Highly Active CNT-Promoted Cu–ZnO–Al2O3 Catalyst for Methanol Synthesis from H2/CO/CO2

In-Situ FTIR Study of CO2 Adsorption and Methanation Mechanism Over Bimetallic Catalyst at Low Temperature

Stabilization of Cu/ZnO Based Catalysts by Nickel Additive in Methanol Decomposition

CuNi Nanoparticles Assembled on Graphene for Catalytic Methanolysis of Ammonia Borane and Hydrogenation of Nitro/Nitrile Compounds

Cu/ZnAl 2 O 4 catalysts prepared by ammonia evaporation method: Improving methanol selectivity in CO 2 hydrogenation via regulation of metal-support interaction

Simultaneously Quantitative and Qualitative Regulation of Active Sites of Ni-Phyllosilicate for Enhanced Co2 Hydrogenation to Methane

Plasma-assisted Fluidized-Bed Atomic Layer Deposition of Pd-Cu Nanoparticles on Porous Powder for CO2 Hydrogenation

Elucidating the Structure-Activity Relationship of the Bimetallic Ni-Cu Catalysts for CO2 Hydrogenation

Depositing the PtNi Nanoparticles on Niobium Oxide to Enhance the Activity and CO-tolerance for Alkaline Methanol Electrooxidation