Abstract:Light alloys are being increasingly investigated as alternatives to ferrous-based engineering components, based on weight considerations. However, in-service applications of such light alloy components often require a surface modification step to enhance their wear and corrosion responses for improved functionality. Thermally sprayed cermet coatings offer an enhanced resistance to wear and corrosion. This work investigates WC-CoCr coatings deposited using two different feedstocks comprising fine and coarse powder size distributions on aluminum alloy and steel substrates using high-velocity air-fuel (HVAF) and high-velocity oxy-fuel (HVOF) spray techniques. The WC-CoCr coatings were HVAF sprayed at various parameters to investigate the relationship between the processing conditions, microstructure, and performance. Microindentation, dry sliding wear, dry sand abrasion, cavitation erosion, and corrosion tests were conducted to assess the performance of the coatings. Despite the qualitative similarities in the microstructures of the coatings, the measured microindentation hardness values were observed to vary, and coatings deposited with higher particle impact velocities showed the highest microhardness between 1400 and 1600 HV0.3. For the three categories of wear investigated, the HVAF coatings showed better resistance than the HVOF coating investigated in this study. The estimated average specific wear rate (SWR) due to sliding wear of the HVOF coating was ~ 16.7 ± 4.0 × 10 −8 mm 3 /Nm compared to that of the most resistant HVAF coating, which exhibited a SWR of ~ 1.7 ± 0.6 × 10 −8 mm 3 /Nm. The cumulative mass loss rate due to the abrasive wear on the HVOF coating reached ~ 1.11 mg/min compared to ~ 0.76 mg/min of the most abrasion-resistant HVAF coating. All coatings showed similar corrosion resistances under the investigated conditions. The combination of wear and corrosion performance of the respective coatings could provide insight into the coating selection for intended applications.

Corrosion Behavior of Hvof Sprayed Hard Face Coatings in Alkaline-Sulfide Solution

Corrosion Behavior of NiCrBSi Coatings Deposited by HVOF Spraying

Assessment of Sulfide Corrosion and Wear Behavior of HVOF-Sprayed Cr 3 C 2 –25nicr Coating on 304 Stainless Steels in H 2 S Environment

Comparison on Long-Term Corrosion Performance of WC-CoCr and Al2O3-TiO2 Ceramic Coatings in Sulphide-Containing 3.5 Wt% NaCl Solution

Corrosion of high-velocity-oxygen-fuel (HVOF) sprayed non-crystalline alloy coating in marine environment

Tribocorrosion behavior of HVOF sprayed WC-based cermet coatings in sodium chloride solution environment in relation to binder phases

Influence of Heat Treatment on Corrosion Resistance of High-Velocity Oxygen-Fuel Sprayed WC-17Co Coatings on 42CrMo Steel

Wear and Corrosion of HVAF and HVOF-Sprayed WC-CoCr Coatings on Aluminum Alloy

Effect of Cobalt and Chromium Content on Microstructure and Properties of WC-Co-Cr Coatings Prepared by High-Velocity Oxy-Fuel Spraying

Erosion-corrosion behaviors of high velocity arc sprayed Fe−Al/Cr<sub>3</sub>C<sub>2</sub> coating

Investigation of Microstructures and Corrosion Resistance of Two Types of AC-HVAF Sprayed WC Coatings

Erosion-corrosion behaviors of high velocity arc sprayed Fe−Al/Cr 3 C 2 coating

A Comparative Study on Wear and Corrosion Behaviour of HVOF- and HVAF-sprayed WC–10Co–4Cr Coatings

Fretting corrosion behavior of WC-10Co-4Cr coating on Inconel 690 alloy by HVOF thermal spraying

Characterization on microstructures and properties of WC-CoCr coating deposited by HVAF and HVOF processes

Uniform Microstructure and Excellent Corrosion Resistance of HVOF-Sprayed CoCrNi Medium-Entropy Alloy Coating in Fluoride Ion Environment

The study of mechanical properties and corrosion behavior of the Fe-based amorphous alloy coatings using high velocity oxygen fuel spraying

Corrosion Behavior of the CoNiCrAlY-Al2O3 Composite Coating Based on Core-Shell Structured Powder Design

Studies on Corrosion Behavior of a Single-Crystal Superalloy and Its Sputtered Nanocrystalline Coatings with Solid NaCl Deposit in O2 + 38 Vol.% H2O Environment at 700 °C

Durability of HVOF Sprayed MoB/CoCr Coating on the 316L Stainless Substrate in Molten 55%Al-Zn-1.5%si Bath

Enhancing the High-Temperature Corrosion Resistance of HVOF-sprayed NiCoCrAlY Coating in Marine Environment by Pt Modification and Pre-Oxidation