Abstract:Abstract Here, numerous oxygen-containing functional groups were grafted onto the surface of CNTs to improve their dispersibility in an electrolyte. The CNTs were characterized by FT-IR, Raman, XPS, FE-SEM, and TEM. The results revealed that the dispersibility of the functionalized CNTs in the composites was better than unfunctionalized CNTs. CNTs/Ni composites were deposited on a copper plate by pulsed electrodeposition and ultrasonic dispersion using an electrolytic bath with CNTs concentrations from 0 to 2 g l −1 . The friction and wear behavior of the composite coatings were assessed using two different methods. In the first method, the coatings were scratched with a progressively higher load from 0–100 N, and the results demonstrate a 10 percent reduction in the coefficient of friction (COF) of the composite compared to pure nickel. The other method involved applying a constant load of 30 N, the COF and microscopic wear mechanism were investigated at different carbon nanotube contents, and the results confirmed that the COF of the composites was gradually reduced with the increase of carbon nanotube mass concentration, and the COF was only 0.343 when the carbon nanotube content was increased to 2 g l −1 . According to the XRD results, increasing the CNTs contents changed the preferred growth orientation. Moreover, the FE-SEM images of the wear surface of the 1 g l −1 CNTs/Ni sample indicated that it had the best wear resistance and showed the smoothest wear trace without apparent cracks. The addition of CNTs enhanced the wear resistance of the nickel matrix due to the superior mechanical strength and lubricating effect of the CNTs. CNTs exposed to the matrix surface reduced the direct contact between the Ni matrix and the friction pair, acted as lubricants, and reduced the wear rate.

Super-Low Friction Nickel Based Carbon Nanotube Composite Coating Electro-Deposited from Eutectic Solvents

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Investigation of the microstructure and tribological properties of CNTs/Ni composites prepared by electrodeposition

Friction and Wear Behavior of Electroless Ni-Based Cnt Composite Coatings

Electroless Preparation and Tribological Properties of Ni-P-Carbon Nanotube Composite Coatings under Lubricated Condition

Preparation of Ni-Cnt Composite Coatings on Aluminum Substrate and Its Friction and Wear Behavior

Friction and wear behaviors of electrodeposited Ni-P-CNTs composite coatings on Al-alloy substrate

Influence of Carbon Nanotube Coatings on Carbon Fiber by Ultrasonically Assisted Electrophoretic Deposition on Its Composite Interfacial Property.

SYNTHESIS AND THE PERFORMANCE OF CARBON NANOTUBES-(Ni-P) COMPOSITES

Enhanced Wear Performance of Cu-Carbon Nanotubes Composite Coatings Prepared by Jet Electrodeposition.

Friction and wear behavior of Ni-based carbon nanotubes composite coatings

Tribological Application of Carbon Nanotubes in a Metal-Based Composite Coating and Composites

Tribological properties of Ni–P-multi-walled carbon nanotubes electroless composite coating

Friction and wear behavior of Ni-P-carbon nanotubes (CNTs) electroless composite coating

Influence on (Ni-P) Electroless Composite Plating with Carbon Nanotubes

Low friction coefficient of superhard nc-TiC/a-C:H nanocomposite coatings deposited by filtered cathodic vacuum arc

Structure and properties of nickel-plated CNTs/Fe-based amorphous composite coatings fabricated by high-speed laser cladding

Effect of sodium dodecyl sulfate (SDS) on the co-deposition and frictional behavior of carbon nanotube/nickel composite layer

Preparation of Electrodeposited Ni-CNTs Nanocomposite Coatings with Highly Wear and Corrosion Resistance Properties

Electrochemical co-deposition of carbon nanotube/Ni composite layer

Friction and Wear Behavior of Electroless Wear-Resistant and Self-Lubricating Ni-P Composite Coatings