Reaction Mechanism and Luminescence Properties of Orange-Red SrAlSi 4 N 7 :Eu 2+ Phosphor for White-Leds

Liu Yuanhong,Zhou Xiaofang,Chen Lei,Zhuang Weidong,Liu Ronghui,Hu Yunsheng

DOI: https://doi.org/10.1016/s1002-0721(17)60903-7

IF: 4.632

2017-01-01

Journal of Rare Earths

Abstract:The well-crystalline SrAlSi 4 N 7 :Eu 2+ phosphor could be synthesized by the solid-state reaction method using different types of Si 3 N 4 raw material.The corresponding reaction mechanism was studied by means of X-ray diffraction(XRD),scanning electron microscopy(SEM),energy-dispersive spectrometry(EDS) and fluorescence spectra.It was found that the structural difference between α-Si 3 N 4 and β-Si 3 N 4 ,and the rearrangement of Si 3 N 4 microstructures at high temperature had an important influence on the formation of SrAlSi 4 N 7 phase.Results showed that the α-β transformation of Si 3 N 4 was included in the synthesis reaction of SrAlSi 4 N 7 .So the reaction mechanism of SrAlSi 4 N 7 :Eu 2+ phosphor should be:α-Si 3 N 4 →β-Si 3 N 4 ;β-Si 3 N 4 +AlN+Sr 2 N→SrAlSi 4 N 7 .The β-Si 3 N 4 seeds addition were actually helpful to the grain growth of α-β transformation of Si 3 N 4 and then increased the synthesis reaction rate of SrAlSi 4 N 7 .Pure SrAlSi 4 N 7 :Eu 2+ phosphor with higher luminous efficacy and better crystal morphology was finally obtained,indicating that the as-synthesized phosphor was an attractive candidate material as an orange-red component for warm white light LEDs.