Tunable emission color and mixed valence state via the modified activator site in the AlN-doped Sr3SiO5:Eu phosphor
Wei Li,Jin Wang,Haoran Zhang,Yingliang Liu,Bingfu Lei,Jianle Zhuang,Jianghu Cui,Mingying Peng,Yue Zhu
DOI: https://doi.org/10.1039/c6ra04387a
IF: 4.036
2016-01-01
RSC Advances
Abstract:Commercially white LEDs have cool white light and a low color rendering index (CRI) due to the absence of red light emission. Considering the respective characteristic luminescence properties of Eu2+ and Eu3+ ions, the combination of the two activators into a single host compound shows promisingly technical feasibility to realize warm w-LEDs with a high CRI but it is still a challenge in practice. Here, we confirmed the mixed europium valence states in Sr(3)Si(1-x)AlxO(5-2x)N(x):Eu phosphors, synthesized by a solid-state reaction method under a H-2/N-2 atmosphere. The crystal structure was characterized by X-ray diffraction and found to crystallize in the Sr3SiO5 phase. The samples show broad excitation bands (250-400 nm) and tunable emission colors from yellow to red, and the CIE chromaticity coordinates of Sr2.97Si1-xAlxO5-2xNx:0.03Eu (x = 0, 0.03, 0.2) were (0.518, 0.474), (0.607, 0.385) and (0.630, 0.367), respectively. The modification of activator sites caused by Al3+-N3(-) replacing Si4+-O2- explained the coexistence of Eu2+/Eu3+ ions, which was demonstrated by Rietveld refinement, photoluminescence analysis and fluorescence lifetime studies. Furthermore, the obtained phosphors also possessed good thermal stabilities. These results suggest that the Sr3Si1-xAlxO5-2xNx:Eu phosphors show potential applications in w-LEDs.