Synthesis and Properties of Novel Red-emitting Phosphor Li_2SrSiO_4:Eu~(3+) for White LED

Z. Y. You

2011-01-01

Abstract:A novel red-emitting phosphor Li2SrSiO4:Eu3+ was synthesized by gel-combustion method,using the metal nitrates as raw materials,and tetraethoxysilane as silica source.The formation process,structure and luminescence properties of as-synthesized Li2SrSiO4:Eu3+ were investigated by FI-IR,XRD and fluorescence spectrophotometer respectively.The results show that the goal product Li2SrSiO4:Eu3+ can be obtained after the precursor obtained from the combustion of dry gel was calcined at 700℃ for 3h.The as-synthesized sample has hexagonal crystal structure and P3121 space group,and unit cell parameter is a=0.5012nm,c=1.2360nm.The excitation spectrum shows a broad band,and the strongest excitation peak is at 396 nm.The strongest emission peak is at 618 nm,which is ascribed to 5D0→7F2 characteristic transition of Eu3+.When the mole fraction x of doped Eu3+ is in the range of 0.04-0.24,the luminescence intensity of the sample increases gradually with the the increase of Eu3+ concentration.It is interesting that no concentration quenching occurs.The synthesized phosphor can absorb near-UV light around 396nm effectively,so it is a suitable red-emitting phosphor for white light-emitting diodes excited by 350-410nm InGaN chip.