Enhanced red luminescence of Ca3Si2−xMxO7:Eu3+ (M = Al, P) phosphors via partial substitution of Si4+ for applications in white light-emitting diodes
Yu-Hao Ma,Xi Gao,Wen-Tao Zhang,Zhen-Rui Yang,Zhou Zhao,Chen Qu
DOI: https://doi.org/10.1007/s12598-023-02334-9
IF: 6.318
2023-09-13
Rare Metals
Abstract:A red-emitting phosphor Ca 2.91 Si 2 O 7 :0.09Eu 3+ with partial Al 3+ /P 5+ substitution on Si 4+ was synthesized via a simple solid-state method, and the effects of the introduction of the M 3+/5+ (M = Al, P) ions on the crystal structure and photoluminescence performance of Ca 2.91 Si 2− x M x O 7 :0.09Eu 3+ phosphors were investigated. The X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS) results revealed that the structure of Ca 3 Si 2 O 7 remained the same after the introduction of Al 3+ and P 5+ ions. The characteristic emission of Eu 3+ -doped Ca 3 Si 2− x M x O 7 phosphors exhibited two main peaks at 617 nm (red) and 593 nm (orange) under excitation at 394 nm, which originated from the 5 D 0 → 7 F 2 and 5 D 0 → 7 F 1 electron transitions of Eu 3+ ions. After the partial substitution of Al 3+ and P 5+ , the red emission intensities of the Ca 2.91 Si 2 O 7 :0.09Eu 3+ phosphors were significantly enhanced by 1.88- and 1.42-fold, respectively, which is attributed to the crystal-field effect around Eu 3+ . Meanwhile, the luminescence intensities of the Ca 2.91 Si 1.96 Al 0.04 O 7 :0.09Eu 3+ and Ca 2.91 Si 1.94 P 0.06 O 7 :0.09Eu 3+ phosphors at 210 °C were 79.36% and 77.53% of those at 30 °C, respectively, indicating their excellent thermal stability. Moreover, the as-prepared Ca 2.91 Si 1.96 Al 0.04 O 7 :0.09Eu 3+ and Ca 2.91 Si 1.94 P 0.06 O 7 :0.09Eu 3+ red-emitting phosphors were combined with a near-ultraviolet chip of 395 nm to fabricate red-light-emitting diode (LED) and white (w)-LED devices with excellent chromaticity features. In summary, Al 3+ /P 5+ -substituted Ca 2.91 Si 2 O 7 :0.09Eu 3+ can serve as red-emitting phosphors for applications in w-LEDs.
materials science, multidisciplinary,metallurgy & metallurgical engineering